Facile formation of superhydrophobic aluminum alloy surface and corrosion-resistant behavior

被引：22
作者：
Feng, Libang [1 ]
Yan, Zhongna [1 ]
Qiang, Xiaohu [1 ]
Liu, Yanhua [1 ]
Wang, Yanping [1 ]
机构：
[1] Lanzhou Jiaotong Univ, Sch Mech Engn, Lanzhou 730070, Peoples R China
来源：
APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING | 2016年 / 122卷 / 03期
基金：
中国国家自然科学基金;
关键词：
NACL AQUEOUS-SOLUTION; ANTIICING PROPERTY; IMMERSION PROCESS; MAGNESIUM ALLOY; OXIDE-FILM; FABRICATION; TRANSPARENT; DISSOLUTION; STABILITY; SUBSTRATE;
D O I：
10.1007/s00339-016-9700-z
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Superhydrophobic surface with excellent corrosion resistance was prepared on aluminum alloy via boiling water treatment and surface modification with stearic acid. Results suggested that the micro-and nanoscale hierarchical structure along with the hydrophobic chemical composition surface confers the aluminum alloy surface with good superhydrophobicity, and the water contact angle and the water sliding angle can reach 156.6 degrees and 3 degrees, respectively. The corrosion resistance of the superhydrophobic aluminum alloy was first characterized by potentiodynamic polarization, and then the long-term corrosion resistance was investigated by immersing the sample in NaCl solution for 90 days. The surface wettability, morphology, and composition before and after immersion were examined, and results showed that the superhydrophobic aluminum alloy surface possessed good corrosion resistance under the experimental conditions, which is favorable for its practical application as an engineering material in seawater corrosion conditions. Finally, the mechanism of the superhydrophobicity and excellent corrosion resistance is deduced.
引用
收藏
页数：14
相关论文
共 35 条
  • [1] Alior W.H., 1968, J HYDRONAUT, V2, P26
  • [2] Wettability of porous surfaces.
    Cassie, ABD
    Baxter, S
    [J]. TRANSACTIONS OF THE FARADAY SOCIETY, 1944, 40 : 0546 - 0550
  • [3] Polystyrene-grafted Al surface with excellent superhydrophobicity and corrosion resistance
    Feng, Libang
    Yan, Zhongna
    Qiang, Xiaohu
    Wang, Yanping
    Liu, Yanhua
    [J]. SURFACE AND INTERFACE ANALYSIS, 2015, 47 (04) : 506 - 513
  • [4] Fabrication of superhydrophobic copper surface with excellent corrosion resistance
    Feng, Libang
    Zhao, Libin
    Qiang, Xiaohu
    Liu, Yanhua
    Sun, Zhiqiang
    Wang, Bei
    [J]. APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, 2015, 119 (01): : 75 - 83
  • [5] Superhydrophobic aluminum alloy surface: Fabrication, structure, and corrosion resistance
    Feng, Libang
    Zhang, Hongxia
    Wang, Zilong
    Liu, Yanhua
    [J]. COLLOIDS AND SURFACES A-PHYSICOCHEMICAL AND ENGINEERING ASPECTS, 2014, 441 : 319 - 325
  • [6] Fabrication of superhydrophobic aluminium alloy surface with excellent corrosion resistance by a facile and environment-friendly method
    Feng, Libang
    Che, Yanhui
    Liu, Yanhua
    Qiang, Xiaohu
    Wang, Yanping
    [J]. APPLIED SURFACE SCIENCE, 2013, 283 : 367 - 374
  • [7] Highly Transparent and UV-Resistant Superhydrophobic SiO2-Coated ZnO Nanorod Arrays
    Gao, Yangqin
    Gereige, Issam
    El Labban, Abdulrahman
    Cha, Dongkyu
    Isimjan, Tayirjan T.
    Beaujuge, Pierre M.
    [J]. ACS APPLIED MATERIALS & INTERFACES, 2014, 6 (04) : 2219 - 2223
  • [8] Superhydrophobic aluminum alloy surfaces prepared by chemical etching process and their corrosion resistance properties
    Huang, Ying
    Sarkar, D. K.
    Chen, X. Grant
    [J]. APPLIED SURFACE SCIENCE, 2015, 356 : 1012 - 1024
  • [9] Superhydrophobic nanostructured ZnO thin films on aluminum alloy substrates by electrophoretic deposition process
    Huang, Ying
    Sarkar, D. K.
    Chen, X-Grant
    [J]. APPLIED SURFACE SCIENCE, 2015, 327 : 327 - 334
  • [10] Rapid Formation of a Superhydrophobic Surface on a Magnesium Alloy Coated with a Cerium Oxide Film by a Simple Immersion Process at Room Temperature and Its Chemical Stability
    Ishizaki, Takahiro
    Saito, Naobumi
    [J]. LANGMUIR, 2010, 26 (12) : 9749 - 9755
1234