Fracture characteristics of thermally exposed 9Cr-1Mo steel after tensile and impact testing at room temperature

被引：62

作者：

Blach, Juraj ^{[1
]}

Falat, Ladislav ^{[1
]}

Sevc, Peter ^{[1
]}

机构：

[1] Slovak Acad Sci, Inst Mat Res, Kosice 04001, Slovakia

来源：

ENGINEERING FAILURE ANALYSIS | 2009年 / 16卷 / 05期

关键词：

9Cr-1Mo steel; Thermal exposition; Microstructure; Tensile and impact properties; Fracture mode; MECHANICAL-PROPERTIES; DUCTILITY;

D O I：

10.1016/j.engfailanal.2008.09.003

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

The paper deals with the fracture analysis of thermally exposed 9Cr-1Mo ferritic steel after tensile and impact testing at room temperature. The temperatures of the thermal expositions were 580, 620, and 650 degrees C, respectively. The duration of annealing experiments varied from 500 to 5000 h. The influence of thermal expositions on Vickers hardness as well as tensile properties was found to be negligible. On the other hand, remarkable effects of the annealing on room temperature impact toughness were observed. Fracture behaviour of the 9Cr-1Mo steel is strongly affected by the presence of precipitates of secondary phases. Fracture surfaces of tensile samples indicate mainly transgranular dimple fracture mechanism. By contrast, the fracture mode of the samples after impact testing is more complex. It shows both - ductile dimple tearing as well as inter-lath decohesion. (C) 2008 Elsevier Ltd. All rights reserved.

引用

页码：1397 / 1403

页数：7

共 15 条

[1] EFFECTS OF TA AND NB ON MICROSTRUCTURES AND MECHANICAL-PROPERTIES OF LOW ACTIVATION FERRITIC 9CR-2W-0.2V STEEL FOR FUSION-REACTOR [J].

ASAKURA, K ;

YAMASHITA, Y ;

YAMADA, T ;

SHIBATA, K .

ISIJ INTERNATIONAL, 1990, 30 (11) :937-946

[2]

Blach J, 2003, KOVOVE MATER, V41, P402

[3]

BLACH J, 2004, HUTN LISTY, V6, P4

[4]

ENGBERG G, 1984, P 2 INT C 2, P697

[5] Microanalysis of two creep resistant 9-12% chromium steels [J].

Hattestrand, M ;

Schwind, M ;

Andren, HO .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1998, 250 (01) :27-36

[6]

HIPPSLEY CA, 1979, ACTA METALL, V28, P869

[7] CHARACTERIZATION OF 9CR-1MOVNB STEEL BY ANOMALOUS SMALL-ANGLE X-RAY-SCATTERING [J].

JEMIAN, PR ;

WEERTMAN, JR ;

LONG, GG ;

SPAL, RD .

ACTA METALLURGICA ET MATERIALIA, 1991, 39 (11) :2477-2487

[8]

Jin Y., 1980, METALL T A, V11A, P277

[9] THE EFFECT OF PHOSPHORUS ON THE DUCTILITY OF 9CR-1MO STEELS [J].

NOBLE, FW ;

SENIOR, BA ;

EYRE, BL .

ACTA METALLURGICA ET MATERIALIA, 1990, 38 (05) :709-717

[10] Basic investigation for life assessment technology of modified 9Cr-1Mo steel [J].

Okamura, H ;

Ohtani, R ;

Saito, K ;

Kimura, K ;

Ishii, R ;

Fujiyama, K ;

Hongo, S ;

Iseki, T ;

Uchida, H .

NUCLEAR ENGINEERING AND DESIGN, 1999, 193 (03) :243-254

← 1 2 →