Real-time studies of phase transformations in Cu-In-Se-S thin films - 3: Selenization of Cu-In precursors

被引:21
作者
Djordjevic, J. [1 ]
Rudigier, E. [1 ]
Scheer, R. [1 ]
机构
[1] Hahn Meitner Inst Berlin GmbH, Div Solar Energy, D-14109 Berlin, Germany
关键词
growth monitoring; phase transformation; XRD; thin film; chalcopyrite; solar cell;
D O I
10.1016/j.jcrysgro.2006.05.080
中图分类号
O7 [晶体学];
学科分类号
0702 ; 070205 ; 0703 ; 080501 ;
摘要
Phase transformations during selenization of thin films of elemental Cu, elemental In, and intermetallic CuxIn with x = (1.8, 1.0, 0.8) are investigated using real-time energy dispersive X-ray diffraction. From the temporal development of the X-ray peak intensities, phase predominance sequence diagrams are constructed including the intensity ratio of the CuK alpha/InK alpha fluorescence lines. It was found that vapor selenization of Cu layers results in the formation of Cu2-xSe. At elevated temperature, linear growth of Cu2-xSe is observed which is interpreted as a surface controlled reaction mechanism. Indium selenization proceeds via the phase sequence In4Se3 -> InSe -> In2Se3. During CuxIn selenization, the transformation sequence towards more Cu-rich intermetallic phases CuIn2 -> Cu11In9 and Cu11In9 -> Cu16In9 precedes the selenization process. During selenization of precursors with x > 1.4, this sequence continues bringing up the intermetallic phases Cu7In3 and alpha-CuIn. The latter are formed at the bottom of the films. Thus, the bottom of the film becomes depleted from Indium by In diffusion. In general, the selenization process is slower than the sulfurization processes investigated in Part 2 of this study. A model is proposed which includes Cu2-xSe as a preliminary precursor for CuInSe2 growth. This Cu2-xSe formation at the surface of the films is proposed to be surface reaction limited and is proposed to be the limiting step for the CuInSe2 formation. Precursors with x <= 1 transform into CuInSe2 with the participation of In-Se phases. (c) 2006 Elsevier BN. All rights reserved.
引用
收藏
页码:218 / 230
页数:13
相关论文
共 34 条
[1]  
AURODIJA FO, 1999, THIN SOLID FILMS, V338, P13
[2]  
AURODIJA FO, 1995, SOL ENERG MAT SOL C, V37, P203
[3]  
BARDELEBEN HJ, 1984, J APPL PHYS, V56, P321
[4]  
Bolcavage A., 1993, J PHASE EQUILIB, V14, P14, DOI DOI 10.1007/BF02652157
[5]   Formation of CuInSe2 by the annealing of stacked elemental layers -: analysis by in situ high-energy powder diffraction [J].
Brummer, A ;
Honkimäki, V ;
Berwian, P ;
Probst, V ;
Palm, J ;
Hock, R .
THIN SOLID FILMS, 2003, 437 (1-2) :297-307
[6]   FREE-ENERGIES AND ENTHALPIES OF POSSIBLE GAS-PHASE AND SURFACE-REACTIONS FOR PREPARATION OF CUINSE2 [J].
CAHEN, D ;
NOUFI, R .
JOURNAL OF PHYSICS AND CHEMISTRY OF SOLIDS, 1992, 53 (08) :991-1005
[7]  
Chakrabarti DJ, 1981, B ALLOY PHASE DIAGRA, V2, P305
[8]   LARGE GRAIN COPPER INDIUM DISELENIDE FILMS [J].
CHU, TL ;
CHU, SS ;
LIN, SC ;
YUE, J .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1984, 131 (09) :2182-2185
[9]   Stable and metastable phase equilibria of the In-Se system [J].
Gödecke, T ;
Haalboom, T ;
Sommer, F .
JOURNAL OF PHASE EQUILIBRIA, 1998, 19 (06) :572-576
[10]  
GOSSLA M, COMMUNICATION