Superplastic behavior of spray-deposited 5083 Al

被引:16
作者
Wu, Y
DelCastillo, L
Lavernia, EJ
机构
[1] Department of Chemical and Biochemical Engineering and Materials Science, University of California, Irvine
来源
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 1997年 / 28卷 / 04期
基金
美国国家科学基金会;
关键词
D O I
10.1007/s11661-997-0235-y
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
A 5083 Al alloy was synthesized using spray deposition processing with N-2 as the atomization gas. It was noted that the grains that were present in as-spray-deposited 5083 Al were equiaxed with an average size of 15.2 mu m. The matrix of the material was supersaturated with Mg and Mn. The as spray-deposited microstructure contained irregular pores with porosity in the range of 0.1 to 5.4 vol pct, depending on spatial location in the preform. The spray-deposited alloy was thermomechanically processed using extrusion and multiple-pass warm rolling to reduce grain size and close porosity. It was observed that spray-deposited 5083 Al exhibited superplasticity following thermomechanical processing by extrusion followed by rolling. Superplasticity was observed in the 500 degrees C to 550 degrees C temperature range and 3 x 10(-5) to 3 x 10(-3) s(-1) strain rate range. The corresponding strain-rate sensitivity factors were in the 0.25 to 0.5 range and increased with decreasing strain rate. A maximum elongation of 465 pct was noted at 550 degrees C and 3 x 10(-5) s(-1). The spray-deposited 5083 Al, thermomechanically processed by direct rolling, exhibited superplasticity in the same temperature and strain rate ranges as those for the extruded and rolled materials. The superplastic elongation of the spray-formed and rolled material was relatively low, being in the range of 250 to 300 pct. The deformation behavior is discussed in light of the presence of porosity in the microstructure.
引用
收藏
页码:1059 / 1068
页数:10
相关论文
共 34 条
[1]   PROCESSING EFFECTS IN SPRAY CASTING OF STEEL STRIP [J].
ANNAVARAPU, S ;
APELIAN, D ;
LAWLEY, A .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1988, 19 (12) :3077-3086
[2]   SPRAY CASTING OF STEEL STRIP - PROCESS ANALYSIS [J].
ANNAVARAPU, S ;
APELIAN, D ;
LAWLEY, A .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1990, 21 (12) :3237-3256
[3]  
BRICKNELL RH, 1979, ACTA METALL MATER, V27, P1303, DOI 10.1016/0001-6160(79)90199-8
[4]   AN ANALYSIS OF CAVITY NUCLEATION IN SUPERPLASTICITY [J].
CHOKSHI, AH ;
MUKHERJEE, AK .
ACTA METALLURGICA, 1989, 37 (11) :3007-3017
[5]   THE INFLUENCE OF ROLLING DIRECTION ON THE MECHANICAL-BEHAVIOR AND FORMATION OF CAVITY STRINGERS IN THE SUPERPLASTIC ZN-22-PERCENT-AL ALLOY [J].
CHOKSHI, AH ;
LANGDON, TG .
ACTA METALLURGICA, 1989, 37 (02) :715-723
[6]   SPRAY FORMING OF ALUMINUM-COPPER ALLOYS [J].
GRANT, PS ;
KIM, WT ;
CANTOR, B .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1991, 134 :1111-1114
[7]   A MATHEMATICAL-MODEL OF THE SPRAY DEPOSITION PROCESS [J].
GUTIERREZMIRAVETE, E ;
LAVERNIA, EJ ;
TRAPAGA, GM ;
SZEKELY, J ;
GRANT, NJ .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1989, 20 (01) :71-85
[8]  
GUTIERREZMIRAVETE E, 1988, INT J RAPID SOLIDIF, V4, P125
[9]   SUPERPLASTICITY IN AN AL-MG-LI-ZR ALLOY AT INTERMEDIATE TEMPERATURES [J].
HALES, SJ ;
MCNELLEY, TR ;
MUNRO, IG .
SCRIPTA METALLURGICA, 1989, 23 (06) :967-972
[10]   RECRYSTALLIZATION AND SUPERPLASTICITY AT 300-DEGREES-C IN AN ALUMINUM-MAGNESIUM ALLOY [J].
HALES, SJ ;
MCNELLEY, TR ;
MCQUEEN, HJ .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1991, 22 (05) :1037-1047