Improvement of environmental stress cracking resistance of polycarbonate by silicone coating

被引：17
|
作者：
Yan, Chenguang [1 ,2 ]
Zhang, Junli [1 ,2 ]
Han, Jian [2 ]
Wang, Xinchao [3 ]
Guan, Zhanshi [1 ,2 ]
Zhang, Lixiang [1 ,2 ]
Liu, Chuntai [2 ]
Shen, Changyu [2 ]
机构：
[1] Zhengzhou Univ, Sch Mat Sci & Engn, 100 Kexue Rd, Zhengzhou 450001, Peoples R China
[2] Zhengzhou Univ, Natl Engn Res Ctr Adv Polymer Proc Technol, 97 Wenhua Rd, Zhengzhou 450002, Peoples R China
[3] Henan Univ Technol, Coll Mechatron Engn, 100 Lianhua St, Zhengzhou 450001, Peoples R China
来源：
POLYMER TESTING | 2017年 / 60卷
基金：
中国国家自然科学基金;
关键词：
Environmental stress cracking; Silicone coating; Stress relaxation; Polycarbonate; BEHAVIOR;
D O I：
10.1016/j.polymertesting.2016.11.007
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
To explore the possibility of using surface coating to reduce environmental stress cracking (ESC) of transparent polycarbonate (PC) parts, silicone coated and SiO2 coated PC were tested in a self-made three-point bending apparatus in the presence of ethanol. The variation of stress with time was recorded, and the surface cracking was observed to evaluate the ESC resistance of samples. Slower stress relaxation rates and fewer surface cracks indicated that silicone coating improved the ESC resistance of PC, but SiO2 coated PC was found to be no better than that of uncoated PC. Silicone coating reduced the absorption of ethanol in PC, weakening the surface plasticization, thus hindering the formation and development of cracks in PC. Nanoindentation test results showed that the mechanical properties such as hardness and elastic modulus of silicone coating are a better match for PC than SiO2 coating. This allows the silicone coating to have a favorable effect in providing continuous protection for PC under the combined action of ethanol and stress. (C) 2016 Elsevier Ltd. All rights reserved.
引用
收藏
页码：6 / 11
页数：6
相关论文
共 50 条
  • [41] Prediction of environmental stress cracking resistance in linear low density polyethylenes
    Maxwell, Antony S.
    Pilkington, Gordon
    POLYMER ENGINEERING AND SCIENCE, 2008, 48 (02): : 360 - 364
  • [42] ENVIRONMENTAL-STRESS CRAZING OF POLYCARBONATE
    MILTZ, J
    DIBENEDETTO, AT
    PETRIE, S
    JOURNAL OF MATERIALS SCIENCE, 1978, 13 (07) : 1427 - 1437
  • [43] Improvement of stress corrosion cracking resistance by low cycle fatigue of a CrNiMoV steel
    Huang, Yu-Hui
    Yang, Fang-Xin
    Wang, Nan
    Zhu, Ming-Liang
    Xuan, Fu-Zhen
    NPJ MATERIALS DEGRADATION, 2023, 7 (01)
  • [44] Improvement of stress corrosion cracking resistance by low cycle fatigue of a CrNiMoV steel
    Yu-Hui Huang
    Fang-Xin Yang
    Nan Wang
    Ming-Liang Zhu
    Fu-Zhen Xuan
    npj Materials Degradation, 7
  • [45] Improvement of Low-Alloy Pipe Steel Sulfide Stress Cracking Resistance
    A. A. Kholodnyi
    Ya. S. Kuznechenko
    Yu. I. Matrosov
    M. V. Il’ichev
    D. I. Yusupov
    Metallurgist, 2019, 63 : 376 - 387
  • [46] Improvement of the resistance to stress corrosion cracking in austenitic stainless steels by cyclic prestraining
    A. Chambreuil-Paret
    T. Magnin
    Metallurgical and Materials Transactions A, 1999, 30 : 1327 - 1331
  • [47] Improvement of the resistance to stress corrosion cracking in austenitic stainless steels by cyclic prestraining
    Chambreuil-Paret, A
    Magnin, T
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1999, 30 (05): : 1327 - 1331
  • [48] Improvement of Low-Alloy Pipe Steel Sulfide Stress Cracking Resistance
    Kholodnyi, A. A.
    Kuznechenko, Ya. S.
    Matrosov, Yu. I.
    Il'ichev, M. V.
    Yusupov, D. I.
    METALLURGIST, 2019, 63 (3-4) : 376 - 387
  • [49] ENVIRONMENTAL-STRESS CRACKING
    CALVERT, PD
    NATURE, 1977, 265 (5590) : 104 - 104
  • [50] ENVIRONMENTAL STRESS CRACKING OF POLYETHYLENE
    TOGGENBURGER, R
    NEWMAN, S
    JOURNAL OF POLYMER SCIENCE PART B-POLYMER LETTERS, 1964, 2 (1PB): : 7 - +
12345