Dry Sliding Wear Behavior of (Cr, Fe)7C3-γ(Cr, Fe) Metal Matrix Composite (MMC) Coatings: The Influence of High Volume Fraction (Cr, Fe)7C3 Carbide

被引：9
|
作者：
Zhou, Y. F. [1 ,2 ]
Qin, G. K. [1 ]
Jiang, P. J. [1 ]
Wang, S. F. [1 ]
Qi, X. W. [1 ]
Xing, X. L. [1 ,2 ]
Yang, Q. X. [2 ]
机构：
[1] Yanshan Univ, Coll Mech Engn, Qinhuangdao 066004, Peoples R China
[2] Yanshan Univ, State Key Lab Metastable Mat Sci & Technol, Qinhuangdao 066004, Peoples R China
来源：
TRIBOLOGY LETTERS | 2018年 / 66卷 / 03期
关键词：
MMC coating; Microstructural evolution; In situ synthesized; (Cr; Fe)(7)C-3; carbide; Wear behavior; CARBON CONTENT; CR; MICROSTRUCTURE; RESISTANCE; ALLOY;
D O I：
10.1007/s11249-018-1053-7
中图分类号：
TQ [化学工业];
学科分类号：
0817 ;
摘要：
The high volume fraction (Cr, Fe)(7)C-3 carbide particle-reinforced metal matrix composite (MMC) coatings with different Cr/C ratios were produced by flux-cored arc welding (FCAW). The in situ synthesized effectiveness of (Cr, Fe)(7)C-3 carbide in the coatings was studied by the aid of CALPHAD and differential scanning calorimeter. The microstructure of the coatings was observed by optical microscope and field emission scanning electron microscope, and their phases were determined by the X-ray diffraction. Meanwhile, the hardness and wear resistance of the coatings were measured. The results show that the (Cr, Fe)(7)C-3 carbide can be in situ synthesized in the coatings. With decreased Cr/C ratio, the in situ synthesized effectiveness of (Cr, Fe)(7)C-3 carbide is improved and the mass fraction of the (Cr, Fe)(7)C-3 carbide is increased. The microstructure of the coatings consists of in situ synthesized (Cr, Fe)(7)C-3 carbide and eutectic (Cr, Fe)(7)C-3/ gamma (Cr, Fe) matrix. The hexagonal-rod-form (Cr, Fe)(7)C-3 carbide can be fractured and segregated from austenite-matrix under a relatively high load force (50 N), and transforms the wear state from two-body-abrasion to three-body-abrasion, which facilitates the coating be seriously abraded and even adhered. The wear resistance of the MMC coatings can be effectively improved by the formation of high volume fraction of (Cr, Fe)(7)C-3 carbide.
引用
收藏
页数：12
相关论文
共 50 条
  • [11] Microstructure and Dry Sliding Wear Behavior of Fe-Based (Cr, Fe)7C3 Composite Coating Fabricated by PTA Welding Process
    Y. L. Yuan
    Z. G. Li
    Journal of Materials Engineering and Performance, 2013, 22 : 3439 - 3449
  • [12] (Fe,Cr)7C3/Fe surface gradient composite: Microstructure, microhardness, and wear resistance
    Ye, Fangxia
    Hojamberdiev, Mirabbos
    Xu, Yunhua
    Zhong, Lisheng
    Yan, Honghua
    Chen, Zhe
    MATERIALS CHEMISTRY AND PHYSICS, 2014, 147 (03) : 823 - 830
  • [13] Planed defects in （Cr,Fe）7C3
    李玉清
    Science in China(Series E:Technological Sciences), 1996, (06) : 584 - 590
  • [14] GROWTH AND PROPERTIES OF MONOVARIANT (FE,CR)-(CR,FE)7C3 EUTECTIC SYSTEM
    VANDENBOOMGAARD, J
    WOLFF, LR
    JOURNAL OF CRYSTAL GROWTH, 1972, 15 (01) : 11 - +
  • [15] STUDY ON PTA CLAD (Cr,Fe)7C3/γ-Fe CERAMAL COMPOSITE COATING
    J.B. Liu1
    in revised form 6 September 2005
    Acta Metallurgica Sinica(English Letters), 2005, (06) : 695 - 700
  • [16] PTA clad (Cr, Fe)7C3/γ-Fe in situ ceramal composite coating
    Liu, Junbo
    Wang, Limei
    Huang, Jihua
    JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING, 2006, 13 (06): : 538 - 541
  • [17] Preparation of in situ (Fe,Cr)7C3/Fe composite coating by centrifugal casting
    Niu, L.
    Xu, Y.
    Wu, H.
    Wang, W.
    SURFACE ENGINEERING, 2011, 27 (08) : 587 - 590
  • [18] PTA clad （Cr,Fe）7C3/γ-Fe in situ ceramal composite coating
    Junbo Liu1)
    Journal of University of Science and Technology Beijing(English Edition), 2006, (06) : 538 - 541
  • [19] POLYTYPIC STRUCTURES OF (CR,FE)7C3 CARBIDES
    KOWALSKI, M
    JOURNAL OF APPLIED CRYSTALLOGRAPHY, 1985, 18 (DEC) : 430 - 435
  • [20] Effect of (Fe,Cr)7C3 carbide orientation on abrasion wear resistance and fracture toughness
    Coronado, J. J.
    WEAR, 2011, 270 (3-4) : 287 - 293
12345