Spray fabrication of superhydrophobic coating on aluminum alloy for corrosion mitigation

被引：52

作者：

Gong, Ao ^{[1
]}

Zheng, Yong ^{[1
]}

Yang, Zhengkai ^{[1
]}

Guo, Xiaoge ^{[1
]}

Gao, Yan ^{[1
]}

Li, Xiaoyu ^{[1
]}

机构：

[1] Nanjing Univ Aeronaut & Astronaut, Coll Mat Sci & Technol, Nanjing 210016, Peoples R China

来源：

MATERIALS TODAY COMMUNICATIONS | 2021年 / 26卷

关键词：

Aluminum alloy; Superhydrophobic coating; Spraying; Silica nanoparticles; Corrosion resistance;

D O I：

10.1016/j.mtcomm.2020.101828

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

A novel superhydrophobic coating was fabricated by spraying with F-SiO2 nanoparticles, epoxy resin adhesive, fluorosilicone varnishes and white fluorinated polyurethane coatings. The wettability, surface roughness, surface morphology and surface chemical group of superhydrophobic coating were characterized. Mechanical stability, corrosion resistance and self-cleaning ability of superhydrophobic coating were examined. Results showed that superhydrophobic coating exhibited excellent water-repellency. The contact angle of superhydrophobic coating was 161.35 degrees and the sliding angle was only 2.0 degrees. The contact angles of superhydrophobic coatings after 20 continuous abrasion cycles, 1.5 h water dripping or 20 tape peeling cycles were all above 150 degrees. Superhydrophobic coating had a significant enhancement in corrosion resistance. The corrosion potential and corrosion current density of coating after 20 d neutral salt spray accelerated corrosion test were -0.54 V and 5.26 x 10(-8) A cm(-2), respectively. Sand adhered to superhydrophobic coating could be easily washed away, which revealed superhydrophobic coating exhibited excellent self-cleaning ability.

引用

页数：10

共 35 条

[1] Purity of the sacred lotus, or escape from contamination in biological surfaces [J].

Barthlott, W ;

Neinhuis, C .

PLANTA, 1997, 202 (01) :1-8

[2] Durable Icephobic Coating for Stainless Steel [J].

Boinovich, Ludmila B. ;

Emelyanenko, Alexandre M. ;

Ivanov, Vladimir K. ;

Pashinin, Andrei S. .

ACS APPLIED MATERIALS & INTERFACES, 2013, 5 (07) :2549-2554

[3] Studies of drag on the nanocomposite superhydrophobic surfaces [J].

Brassard, Jean-Denis ;

Sarkar, D. K. ;

Perrona, Jean .

APPLIED SURFACE SCIENCE, 2015, 324 :525-531

[4] Wettability of porous surfaces. [J].

Cassie, ABD ;

Baxter, S .

TRANSACTIONS OF THE FARADAY SOCIETY, 1944, 40 :0546-0550

[5] Nanocasting Technique to Prepare Lotus-leaf-like Superhydrophobic Electroactive Polyimide as Advanced Anticorrosive Coatings [J].

Chang, Kung-Chin ;

Lu, Hsin-I ;

Peng, Chih-Wei ;

Lai, Mei-Chun ;

Hsu, Sheng-Chieh ;

Hsu, Min-Hsiang ;

Tsai, Yuan-Kai ;

Chang, Chi-Hao ;

Hung, Wei-I ;

Wei, Yen ;

Yeh, Jui-Ming .

ACS APPLIED MATERIALS & INTERFACES, 2013, 5 (04) :1460-1467

[6]

El Abedin SZ, 2001, J APPL ELECTROCHEM, V31, P711

[7] Water-repellent legs of water striders [J].

Gao, XF ;

Jiang, L .

NATURE, 2004, 432 (7013) :36-36

[8] Biocompatibility, corrosion resistance and antibacterial activity of TiO2/CuO coating on titanium [J].

He, Xiaojing ;

Zhang, Guannan ;

Wang, Xin ;

Hang, Ruiqiang ;

Huang, Xiaobo ;

Qin, Lin ;

Tang, Bin ;

Zhang, Xiangyu .

CERAMICS INTERNATIONAL, 2017, 43 (18) :16185-16195

[9] Electrochemical properties and corrosion protection of organosilane self-assembled monolayers on aluminum 2024-T3 [J].

Hintze, PE ;

Calle, LM .

ELECTROCHIMICA ACTA, 2006, 51 (8-9) :1761-1766

[10] The electrochemical behavior of nanocomposite organic coating based on clay nanotubes filled with green corrosion inhibitor through a vacuum-assisted procedure [J].

Izadi, M. ;

Shahrabi, T. ;

Mohammadi, I. ;

Ramezanzadeh, B. ;

Fateh, A. .

COMPOSITES PART B-ENGINEERING, 2019, 171 :96-110

← 1 2 3 4 →