Organic solvent-saving preparation of water glass based aerogel granules under ambient pressure drying

被引：45

作者：

Huang, Yajun ^{[1
,2
]}

He, Song ^{[1
]}

Feng, Mengmeng ^{[1
]}

Dai, Huaming ^{[1
]}

Pan, Yuelei ^{[2
]}

Cheng, Xudong ^{[2
]}

机构：

[1] Wuhan Univ Technol, Sch Safety Sci & Emergency Management, Luoshi Rd 122, Wuhan 430070, Peoples R China

[2] Univ Sci & Technol China, State Key Lab Fire Sci, Hefei 230027, Anhui, Peoples R China

来源：

JOURNAL OF NON-CRYSTALLINE SOLIDS | 2019年 / 521卷

关键词：

Water glass; Ethanol; Sol-gel process; Hexamethyldisiloxane; Silica aerogel; SOL-GEL PROCESS; SILICA AEROGELS; THERMAL-CONDUCTIVITY; PHYSICAL-PROPERTIES; SODIUM-SILICATE; XEROGELS;

D O I：

10.1016/j.jnoncrysol.2019.119507

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

An organic solvent-saving method of preparing silica aerogel is reported. The silica aerogel was made from water glass (WG) and used as the solvent. Na+ was removed through ion exchange; prior to this ion exchange, concentrated hydrochloric acid (HCl) was added to the WG solution. The sol pH was adjusted to similar to 1 to suppress the condensation to the maximum extent. Ethanol was added to the sol after ion exchange. Surface modification was conducted with the assistance of hexamethyldisiloxane, which was catalyzed by HCl. The entire process can be finished in 6 h. The overall consumption of organic solvent is much lower than that in the previous preparation route. Characterization results indicate that the resulted silica aerogel has a uniform mesoporous structure and low thermal conductivity (0.0237-0.0245 W/m.K at 1 atm).

引用

页数：7

共 43 条

[1]

Albertina Cabanas E. E., 2005, CHEM MATER, V17, P9

[2]

[Anonymous], 1990, Sol-gel science - the Physics and Chemistry of Sol-Gel Processing

[3]

[Anonymous], 1978, The Chemistry of Silica: Solubility, Polymerization, Colloid and Surface Properties and Biochemistry

[4] Optically transparent silica aerogels based on sodium silicate by a two step sol-gel process and ambient pressure drying [J].

Bangi, Uzma K. H. ;

Jung, In-Keun ;

Park, Chang-Sun ;

Baek, Seungsu ;

Park, Hyung-Ho .

SOLID STATE SCIENCES, 2013, 18 :50-57

[5] Studies on the porosity of SiO2-aerogel inverse opals synthesised in supercritical CO2 [J].

Cabanas, Albertina ;

Enciso, Eduardo ;

Carbajo, M. Carmen ;

Torralvo, Maria J. ;

Pando, Concepcion ;

Renuncio, Juan Antonio R. .

MICROPOROUS AND MESOPOROUS MATERIALS, 2007, 99 (1-2) :23-29

[6] Monolithic Nanoporous Crystalline Aerogels [J].

Daniel, Christophe ;

Longo, Simona ;

Ricciardi, Rosa ;

Reverchon, Ernesto ;

Guerra, Gaetano .

MACROMOLECULAR RAPID COMMUNICATIONS, 2013, 34 (15) :1194-1207

[7] Optimized synthesis of ambient pressure dried thermal insulating silica aerogel powder from non-ion exchanged water glass [J].

De Pooter, Steve ;

Latre, Steven ;

Desplentere, Frederik ;

Seveno, David .

JOURNAL OF NON-CRYSTALLINE SOLIDS, 2018, 499 :217-226

[8]

[邓凌峰 Deng Lingfeng], 2013, [材料导报, Materials Review], V27, P75

[9] NMR and IR spectroscopy of silica aerogels with different hydrophobic characteristics [J].

El Rassy, H ;

Pierre, AC .

JOURNAL OF NON-CRYSTALLINE SOLIDS, 2005, 351 (19-20) :1603-1610

[10]

Guo X. Z., 2018, MOLECULES, V23, P14

← 1 2 3 4 5 →