Effect of cooling rates on as-cast microstructures of U-5.4Nb alloys

被引:2
作者
Ma, Rong [1 ]
Liu, Tingyi [1 ]
Hu, Guichao [1 ]
Wu, Jun [1 ]
Ren, Zhiyong [1 ]
Chen, Dong [1 ]
Li, Yufei [1 ]
Luo, Chao [1 ]
机构
[1] China Acad Engn Phys, Mianyang 621900, Sichuan, Peoples R China
关键词
Solidification; Microstructure; Dendrite; Microsegregation; SOLUTE REDISTRIBUTION; PHASE-TRANSFORMATIONS; NEUTRON-DIFFRACTION; THERMAL-ANALYSIS; DENDRITE GROWTH; ELASTIC-MODULUS; GAMMA-PHASE; NIOBIUM; NB; SOLIDIFICATION;
D O I
10.1016/j.jnucmat.2020.152498
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
As-cast microstructural features of a U-5.4Nb alloy, including average grain size, dendrite structure, inclusion evolution behavior, solute (Nb) distribution and micromechanical properties were investigated with respect to a diverse number of calculated cooling rates in this paper. Various solidification techniques, including suction casting, arc remelting and induction melting followed by argon cooling, were employed to obtain wide ranges of cooling rates between 90 K/s and 9.9 x 10(5) K/s. Average grain sizes of suction cast samples decreased from 16.8 mu m to 4.35 mu m with increasing cooling rates. Similarly, inclusion evolution behavior was shown to refine in size with the increase of cooling rates. Fully developed dendrites inside the argon-cooled sample at a low cooling rate consisted of primary dendrite arms, secondary dendrite arms and tertiary dendrite arms that exhibited a fascinating dendrite structure with hexagonal symmetry. In addition, the segregation ratios of niobium decreased with decreasing cooling rates. Furthermore, the nanoindentation test indicated that the segregation of niobium had a significant influence on the mechanical properties of the dendrite arms and interdendritic regions. The elastic modulus and hardness for the primary dendrite arm, the secondary dendrite arm, and the interdendritic region were 61 GPa and 3.6 GPa, 62 GPa and 3.3 GPa, and 113 GPa and 6.5 GPa, respectively. (C) 2020 Elsevier B.V. All rights reserved.
引用
收藏
页数:13
相关论文
共 82 条
[1]  
Aikin R M J, 2018, LAUR1829233 LOS AL N
[2]  
Aikin R.M.J., 2017, LAUR1729064 LOS AL N
[3]  
Aikin R.M.J., 2015, LAUR1521924 LOS AL N
[4]  
Aikin R.M.J., 2019, LAUR1920257 LOS AL N
[5]   Thermal analysis during continuous casting process using effective heat capacity method [J].
Amin, MR .
JOURNAL OF THERMOPHYSICS AND HEAT TRANSFER, 2000, 14 (02) :170-176
[6]   PHASES METASTABLES DANS LES ALLIAGES URANIUM-NIOBIUM [J].
ANAGNOSTIDIS, M ;
COLOMBIE, M ;
MONTI, H .
JOURNAL OF NUCLEAR MATERIALS, 1964, 11 (01) :67-76
[7]   Solidification microstructures and solid-state parallels: Recent developments, future directions [J].
Asta, M. ;
Beckermann, C. ;
Karma, A. ;
Kurz, W. ;
Napolitano, R. ;
Plapp, M. ;
Purdy, G. ;
Rappaz, M. ;
Trivedi, R. .
ACTA MATERIALIA, 2009, 57 (04) :941-971
[8]  
Avery J.G., 1974, RFP2067 DOW CHEM COR
[9]   CONSTITUTION OF LOW CARBON U-C ALLOYS [J].
BLUMENTHAL, B .
JOURNAL OF NUCLEAR MATERIALS, 1960, 2 (03) :197-208
[10]  
BOWER TF, 1966, T METALL SOC AIME, V236, P624