Low-cycle fatigue behaviour of ductile closed-cell aluminium alloy foams

被引：43

作者：

Linul, E. ^{[1
]}

Serban, D. A. ^{[1
,2
]}

Marsavina, L. ^{[1
]}

Kovacik, J. ^{[3
]}

机构：

[1] Politeh Univ Timisoara, Dept Mech & Strength Mat, Timisoara 300222, Romania

[2] Politeh Univ Timisoara, Res Inst Renewable Energy, Timisoara 300777, Romania

[3] Slovak Acad Sci, Inst Mat Machine Mech, Bratislava 84513, Slovakia

来源：

FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES | 2017年 / 40卷 / 04期

关键词：

closed-cell aluminium foams; compression-compression cyclic tests; low-cycle fatigue; plastic collapse; structure irregularity; CRACK PROPAGATION; STRENGTH; LIFE; FAILURE; STEEL;

D O I：

10.1111/ffe.12535

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

This work investigates the fatigue response of a class of ductile closed-cell aluminium alloy foams, known by their commercial name Alulight M8. In order to determine the yield stress of the used foams, preliminary experimental tests were performed, at room temperature, in monotonic compression on cylindrical specimens of 25mm diameter and 25mm height, with a loading speed of 10 mm/min. Fatigue tests were performed in uniaxial compression on cylindrical specimens (25mmx 25mm) with a stress ratio of R = 0.1, at a frequency of 10 Hz. The peak stress was varied from 110 to 135% of the yield stress in compression. Tested specimens were cut from the same cylindrical bar, and the density of the investigated material was 500 kg/m(3) +/- 10%, or a total of 18 specimens being investigated. With the gathered experimental data, S-N curve was generated, and the effect of cellular structure (e.g. structure irregularity-the number and the size of cells) being investigated and discussed.

引用

页码：597 / 604

页数：8

共 34 条

[31] Experimental determination of mechanical properties of aluminium foams using Digital Image Correlation [J].

Voiconi, Tudor ;

Linul, Emanoil ;

Marsavina, Liviu ;

Kovacik, Jaroslav ;

Knec, Marcin .

PROCEEDINGS OF THE 14TH SYMPOSIUM ON EXPERIMENTAL STRESS ANALYSIS AND MATERIALS TESTING, 2014, 601 :254-+

[32] Fatigue properties of aluminium foams at high numbers of cycles [J].

Zettl, B ;

Mayer, H ;

Stanzl-Tschegg, SE ;

Degischer, HP .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2000, 292 (01) :1-7

[33] Fatigue properties of Al-1Mg-0.6Si foam at low and ultrasonic frequencies [J].

Zettl, B ;

Mayer, H ;

Stanzl-Tschegg, SE .

INTERNATIONAL JOURNAL OF FATIGUE, 2001, 23 (07) :565-573

[34] Experimental investigation of the fatigue of closed-cell aluminum alloy foam [J].

Zhao, M. D. ;

Fan, Xueling ;

Fang, Qin-Zhi ;

Wang, T. J. .

MATERIALS LETTERS, 2015, 160 :68-71

← 1 2 3 4 →