Partial oxidation of simulated hot coke oven gas to syngas over Ru-Ni/Mg(Al)O catalyst in a ceramic membrane reactor

Hydrogen amplification from simulated hot coke oven gas (HCOG) was investigated in a BaCo0.7Fe0.2Nb0.1O3-delta (BCFNO) membrane reactor combined with a Ru-Ni/Mg(Al)O catalyst by the partial oxidation of hydrocarbon compounds under atmospheric pressure. Under optimized reaction conditions, the dense oxygen permeable membrane had an oxygen permeation flux around 13.3 ml/(cm(2).mm). By reforming of the toluene and methane, the amount of H-2 in the reaction effluent gas was about 2 times more than that of original H-2 in simulated HCOG. The Ru-Ni/Mg(Al)O catalyst used in the membrane reactor possessed good catalytic activity and resistance to coking. After the activity test, a small amount of whisker carbon was observed on the used catalyst, and most of them could be removed in the hydrogen-rich atmosphere, implying fiat the carbon deposition formed on the catalyst might be a reversible process.