Influences of Cu in steel on the formation of alloy layer in hot-dip galvanizing

被引：3

作者：

Komatsu, A

Ando, A

Kittaka, T

机构：

[1] Coating and Coated Prod. Lab.-1, Surface Treatment Department, Nisshin Steel Co., Ltd., Sakai, Osaka-fu 592, Ishizu-Nishimachi

来源：

ISIJ INTERNATIONAL | 1997年 / 37卷 / 03期

关键词：

hot-dip galvanizing; pickling; reduction heating; intermetallic compound layer; equilibrium; phase diagram; diffusion; solubility; out-burst;

D O I：

10.2355/isijinternational.37.283

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The influence of Cu in steel on hot-dip galvanizing of hot rolled steel was studied. We investigated the formation of the alloy layer formed at the overlay-substrate interface. On Cu-Ti-added steel, the formation of delta(1) phase was promoted, while Fe2Al5 was the main phase on the usual Ti-added steel. We concluded that this phenomenon was caused by the dissolution of Cu into the Zn bath that had deposited on the surface during pickling, and suggested that the dissolution of Cu should decrease the activity of Al and make Fe2Al5 less stable than that of Ti-added steel, which caused the easy precipitation of delta(1).

引用

页码：283 / 289

页数：7

共 12 条

[1]

BRACHET JC, 1991, RAPPORT DEA

[2]

*FED REP GERM, 1992, TERN ALL, V5, P505

[3]

*FED REP GERM, 1992, TERN ALL, V5, P92

[4] ALUMINUM-RICH ALLOY LAYERS FORMED DURING HOT DIP GALVANIZING OF LOW-CARBON STEEL [J].

HARVEY, GJ ;

MERCER, PD .

METALLURGICAL TRANSACTIONS, 1973, 4 (02) :619-621

[5]

Hirose Y., 1982, TETSU TO HAGANE, V68, P658

[6]

LIN CS, 1995, GALVATECH 95, P335

[7]

MARDER AR, 1994, PHYSICAL METALLURGY, P41

[8] FORMATION BEHAVIOR OF ALLOY LAYER IN INITIAL-STAGES OF GALVANIZING [J].

SAITO, M ;

UCHIDA, Y ;

KITTAKA, T ;

HIROSE, Y ;

HISAMATSU, Y .

TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1991, 77 (07) :947-954

[9]

UREDNICE.M, 1973, Z METALLKD, V64, P899

[10]

UREDNICEK M, 1973, Z METALLKD, V64, P419

← 1 2 →