Effect of different carbon nano-fillers on rheological properties and lap shear strength of epoxy adhesive joints

In this work, the rheological properties, thermal stability and the lap shear strength of epoxy adhesive joints reinforced with different carbon nano-fillers such as multi-walled carbon nanotubes (CNT), graphene nanoplatelets (GNP) and single-walled carbon nanohorns (CNH) have been studied. The nano fillers were dispersed homogeneously using Brabender (R) Plasti-Corder (R). The epoxy pre-polymer with and without the nano-fillers exhibited shear thinning behavior. The nano-filler epoxy mixtures exhibited a viscoplastic behavior which was analyzed using Casson's model. Thermo-gravimetric analysis indicated an increase in the thermal stability of the epoxy with the addition of carbon nano-fillers. Carbon nano fillers resulted in increased lap shear strength having high Weibull modulus. The joint strength increased by 53%, 49% and 46% with the addition of 1 wt.% CNT, 0.5 wt.% GNP and 0.5 wt.% CNH, respectively. The strength of the joints having high filler content (>1 wt.%) was limited by mixed mode type of failure. (C) 2015 Elsevier Ltd. All rights reserved.