Preparation of γ-Al2O3 film by high temperature transformation of nanosized γ-AlOOH precursors

被引：26
|
作者：
Mathieu, Yannick [1 ]
Vidal, Loic [1 ]
Valtchev, Valentin [1 ]
Lebeau, Benedicte [1 ]
机构：
[1] Univ Haute Alsace, ENSCMu 3, Equipe Mat Porosite Controlee MPC, IS2M,LRC CNRS 7228, F-68093 Mulhouse, France
来源：
NEW JOURNAL OF CHEMISTRY | 2009年 / 33卷 / 11期
关键词：
FIBROUS BOEHMITE SOL; ALUMINA MEMBRANE; SUSPENSIONS; FABRICATION; MORPHOLOGY; TRANSPORT; COATINGS; SURFACE; RODS;
D O I：
10.1039/b9nj00351g
中图分类号：
O6 [化学];
学科分类号：
0703 ;
摘要：
Mesoporous boehmite (gamma-AlOOH) and gamma-alumina (gamma-Al2O3) self-supported films were prepared by high temperature transformation of gamma-AlOOH precursor fibers. A polymer, sodium polyacrylate, was used as a size/ morphology controlling agent yielding to a stable colloidal suspension of boehmite ribbon-like fibers after a 168 h hydrothermal treatment at 160 degrees C. The slow evaporation of the solvent leads to gamma-AlOOH film without any cracks and pinholes. The gamma-Al2O3 film, obtained after calcination of the gamma-AlOOH film, exhibit a high thermal stability up to 1000 degrees C and two distinct kinds of mesopores with average diameters of 20-30 angstrom and 50 angstrom. Structural and textural properties of these films confer them interesting properties for filtration processes.
引用
收藏
页码：2255 / 2260
页数：6
相关论文
共 50 条
  • [41] A novel method for the preparation of Cu/Al2O3 nanocomposite
    Wen, Yueli
    Huang, Wei
    Wang, Bin
    APPLIED SURFACE SCIENCE, 2012, 258 (07) : 2935 - 2938
  • [42] Preparation of Al2O3 and MgAl2O4-based samples with tailored macroporous structures
    Araujo, Guilherme T.
    Brito, Thiago S.
    Souza, Douglas F.
    Silv, Alysson M. A.
    Nunes, Eduardo H. M.
    Houmard, Manuel
    CERAMICS INTERNATIONAL, 2018, 44 (01) : 580 - 587
  • [43] Effects of PVP on the preparation of nanosized Al2O3 supported Ni catalysts by polyol method for catalytic partial oxidation of methane
    Bayrakdar, Ezgi
    Altincekic, Tuba Gurkaynak
    Oksuzomer, M. Ali Faruk
    FUEL PROCESSING TECHNOLOGY, 2013, 110 : 167 - 175
  • [44] Effect of Al2O3 fibers on the high-temperature stability of silicone elastomer
    Yao, Yiying
    Lu, Guo-Quan
    Boroyevich, Dushan
    Ngo, Khai D. T.
    POLYMER, 2014, 55 (16) : 4232 - 4240
  • [45] Valorization of Aluminum Chips into γ-Al2O3 and η-Al2O3 with High Surface Areas via the Precipitation Route
    Jraba, Nawel
    Tounsi, Hassib
    Makhlouf, Thabet
    WASTE AND BIOMASS VALORIZATION, 2018, 9 (06) : 1003 - 1014
  • [46] Design of the Metal Precursors Molecular Structures in Impregnating Solutions for Preparation of Efficient NiMo/Al2O3 Hydrodesulfurization Catalysts
    Li Huifeng
    Li Mingfeng
    Chu Yang
    Liu Feng
    Nie Hong
    CHINA PETROLEUM PROCESSING & PETROCHEMICAL TECHNOLOGY, 2015, 17 (04) : 37 - 45
  • [47] Characterisation of high-temperature annealing effects on α-Al2O3(0001) substrates
    Qi, BingCui
    Agnarsson, B.
    Jonsson, K.
    Olafsson, S.
    Gislason, H. P.
    PROCEEDINGS OF THE 17TH INTERNATIONAL VACUUM CONGRESS/13TH INTERNATIONAL CONFERENCE ON SURFACE SCIENCE/INTERNATIONAL CONFERENCE ON NANOSCIENCE AND TECHNOLOGY, 2008, 100
  • [48] Hydrodeoxygenation of methyl palmitate over sulfided Mo/Al2O3, CoMo/Al2O3 and NiMo/Al2O3 catalysts
    Deliy, Irina V.
    Vlasova, Evgenia N.
    Nuzhdin, Alexey L.
    Gerasimov, Evgeny Yu
    Bukhtiyarova, Galina A.
    RSC ADVANCES, 2014, 4 (05): : 2242 - 2250
  • [49] Phase transformation in κ- and γ-Al2O3 coatings on cutting tool inserts
    Trinh, D. H.
    Back, K.
    Pozina, G.
    BlomqviSt, H.
    Selinder, T.
    Collin, M.
    Reineck, I.
    Hultman, L.
    Hogberg, H.
    SURFACE & COATINGS TECHNOLOGY, 2009, 203 (12) : 1682 - 1688
  • [50] Controllable preparation of novel Fe2O3/flake α-Al2O3 pearlescent pigments with high coating ratio
    Zhu, Huaqiang
    Long, Kailin
    Liu, Fengkun
    Su, Xiangdong
    CERAMICS INTERNATIONAL, 2023, 49 (14) : 24047 - 24055
12345