The effect of modified and nonmodified carbon additives on the physicomechanical properties of cement composites

被引：0

作者：

Skowronski, Jan M. ^{[1
]}

Slosarczyk, Agnieszka ^{[1
]}

机构：

[1] Politechn Poznanska, Inst Chem & Elektrochem Tech, PL-60965 Poznan, Poland

来源：

PRZEMYSL CHEMICZNY | 2006年 / 85卷 / 8-9期

关键词：

D O I：

暂无

中图分类号：

O6 [化学];

学科分类号：

0703 ;

摘要：

Short 13 x 700- mu m C fibers and mesocarbon microbeads oxidized 3 hrs./80 degrees C and 24 hrs./room temp. with conc. HNO3 and dried, were added, 0.5 and 1%, to cement mortars. The hot-oxidized C was superior as a modifier of cement-C composites. Spherical C raised the bending and the compression strengths and the oxidized C fibers (1%) enhanced the bending strength. Nonmodified C (0.5%) increased the shrinkage of the composites.

引用

页码：862 / 864

页数：3

共 6 条

[1] Low-drying-shrinkage concrete containing carbon fibers [J].

Chen, PW ;

Chung, DDL .

COMPOSITES PART B-ENGINEERING, 1996, 27 (3-4) :269-274

[2]

Chung D.D.L., 1994, Carbon Fiber Composites

[3]

OSIECKA E, 2000, WYBRANE ZAGADNIENIA

[4]

SKOWRONSKI JM, 2005, KARBO, V4, P273

[5]

XU Y, 2001, CARBON, V39, P337

[6] Comparison of short carbon fibre surface treatments on epoxy composites - I. Enhancement of the mechanical properties [J].

Zhang, H ;

Zhang, Z ;

Breidt, C .

COMPOSITES SCIENCE AND TECHNOLOGY, 2004, 64 (13-14) :2021-2029

← 1 →