Electrochemical study the corrosion behaviour of carbon steel in mortars under compressive and tensile stresses

被引：53

作者：

Feng, Xingguo ^{[1
]}

Lu, Xiangyu ^{[2
]}

Zuo, Yu ^{[3
]}

Zhuang, Ning ^{[1
]}

Chen, Da ^{[1
]}

机构：

[1] Hohai Univ, Jiangsu Key Lab Coast Ocean Resources Dev & Envir, Nanjing 210098, Jiangsu, Peoples R China

[2] Jiangsu Univ Sci & Technol, Sch Mat Sci & Engn, Zhenjiang 212003, Jiangsu, Peoples R China

[3] Beijing Univ Chem Technol, Sch Mat Sci & Engn, Beijing 100029, Peoples R China

来源：

CORROSION SCIENCE | 2016年 / 103卷

基金：

中国国家自然科学基金;

关键词：

Concrete; Steel reinforced concrete; Polarization; EIS; Interfaces; REINFORCED-CONCRETE; PASSIVE FILM; RESISTANCE; TEMPERATURE; PERFORMANCE; ENVIRONMENT; BEAMS; CRACK; BOND;

D O I：

10.1016/j.corsci.2015.11.006

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The influence of compressive and tensile stresses on the corrosion behaviour of the rebar in mortars was investigated. The corrosion of the rebar intensified with increasing magnitude of the stress. Results of electrochemical impedance spectroscopy and the observed corrosion state indicated that the stress induced corrosion of the rebar resulted mainly from degradation of the concrete/rebar interface. For the same magnitude of stress, the rebar in the compressed sample was more severely corroded than that in the tensile sample. In addition, modes were proposed to illustrate the different failure patterns of the concrete/rebar interface, owing to the action of the stresses. (C) 2015 Elsevier Ltd. All rights reserved.

引用

页码：66 / 74

页数：9

共 36 条

[11] Electrochemical impedance behavior of mortar subjected to a sulfate environment - A comparison with chloride exposure models [J].

Braganca, Mariana O. G. P. ;

Portella, Kleber F. ;

Bonato, Marcelle M. ;

Marino, Claudia E. B. .

CONSTRUCTION AND BUILDING MATERIALS, 2014, 68 :650-658

[12] Modelling of interaction between corrosion-induced concrete cover crack and steel corrosion rate [J].

Cao, Chong ;

Cheung, Moe M. S. ;

Chan, Ben Y. B. .

CORROSION SCIENCE, 2013, 69 :97-109

[13] Electronic structure and pitting susceptibility of passive film on carbon steel [J].

Cheng, YF ;

Luo, JL .

ELECTROCHIMICA ACTA, 1999, 44 (17) :2947-2957

[14] The electrochemical behaviour of steel rebars in concrete: an Electrochemical Impedance Spectroscopy study of the effect of temperature [J].

Deus, J. M. ;

Diaz, B. ;

Freire, L. ;

Novoa, X. R. .

ELECTROCHIMICA ACTA, 2014, 131 :106-115

[15] Corrosion behavior of epoxy/zinc duplex coated rebar embedded in concrete in ocean environment [J].

Dong, ShiGang ;

Zhao, Bing ;

Lin, Changjian ;

Du, RongGui ;

Hu, RongGang ;

Zhang, Gregory Xiaoge .

CONSTRUCTION AND BUILDING MATERIALS, 2012, 28 (01) :72-78

[16] Effect of corrosion on bond in reinforced concrete under cyclic loading [J].

Fang, CQ ;

Gylltoft, K ;

Lundgren, K ;

Plos, M .

CEMENT AND CONCRETE RESEARCH, 2006, 36 (03) :548-555

[17] Crack profile in RC, R/FRCC and R/HPFRCC members in tension [J].

Fantilli, Alessandro P. ;

Mihashi, Hirozo ;

Vallini, Paolo .

MATERIALS AND STRUCTURES, 2007, 40 (10) :1099-1114

[18] The degradation of passive film on carbon steel in concrete pore solution under compressive and tensile stresses [J].

Feng, Xingguo ;

Zuo, Yu ;

Tang, Yuming ;

Zhao, Xuhui ;

Lu, Xiangyu .

ELECTROCHIMICA ACTA, 2011, 58 :258-263

[19]

Freund L. B., 2004, Thin Film Materials: Stress, Defect Formation and Surface Evolution

[20]

Gao R., 2012, J MATER CIVIL ENG, V25, P39

← 1 2 3 4 →