Influence of surface chemistry on photoluminescence from deuterium-passivated silicon nanocrystals

被引:8
作者
Salivati, Navneethakrishnan [1 ]
Shuall, Nimrod [2 ]
Baskin, Emanuel [2 ]
Garber, Valery [2 ]
McCrate, Joseph M. [1 ]
Ekerdt, John G. [1 ]
机构
[1] Univ Texas Austin, Dept Chem Engn, Austin, TX 78712 USA
[2] DC Sirica Ltd, IL-36680 Nesher, Israel
关键词
CHEMICAL-VAPOR-DEPOSITION; SI NANOCRYSTALS; POROUS SILICON; QUANTUM DOTS; HYDROGEN; NANOPARTICLES; SI(100);
D O I
10.1063/1.3224952
中图分类号
O59 [应用物理学];
学科分类号
摘要
Although silicon (Si) nanostructures exhibit size dependent light emission, which can be attributed to quantum confinement, the role of surface passivation is not fully understood. Si nanocrystals less than 6 nm in diameter are grown on SiO2 surfaces in an ultrahigh vacuum chamber using hot wire chemical vapor deposition. The surface chemistry of deuterium-passivated Si nanocrystals is studied using temperature programed desorption to follow the formation of surface deuterides and amorphization of Si nanocrystals. The influence of the surface deuteride species and amorphization on the photoluminescence (PL) emitted from Si nanocrystals is reported for an excitation wavelength of 405 nm. No PL is observed from the as-grown unpassivated nanocrystals. The as-grown surfaces are exposed to atomic deuterium at 375 K and PL is measured at 310-315 K. As the deuterium dose is increased, the PL intensity also begins to increase. This can be associated with increasing amounts of mono-, di-, and trideuteride species on the nanocrystal surface, which results in better passivation of the dangling bonds. At high deuterium doses, the surface structure breaks down and amorphization of the top layer of the nanocrystal takes place. Amorphization reduces the PL intensity. Finally, as the nanocrystal size is varied, the PL peak shifts, which is characteristic of quantum confinement. (C) 2009 American Institute of Physics. [doi:10.1063/1.3224952]
引用
收藏
页数:8
相关论文
共 29 条
[1]   SILICON QUANTUM WIRE ARRAY FABRICATION BY ELECTROCHEMICAL AND CHEMICAL DISSOLUTION OF WAFERS [J].
CANHAM, LT .
APPLIED PHYSICS LETTERS, 1990, 57 (10) :1046-1048
[2]   H-INDUCED SURFACE RESTRUCTURING ON SI(100) - FORMATION OF HIGHER HYDRIDES [J].
CHENG, CC ;
YATES, JT .
PHYSICAL REVIEW B, 1991, 43 (05) :4041-4045
[3]   Effect of hydrogen passivation on charge storage in silicon quantum dots embedded in silicon nitride film [J].
Cho, CH ;
Kim, BH ;
Kim, TW ;
Park, SJ ;
Park, NM ;
Sung, GY .
APPLIED PHYSICS LETTERS, 2005, 86 (14) :1-3
[4]   INTERPRETATION OF THE TEMPERATURE-DEPENDENCE OF THE STRONG VISIBLE PHOTOLUMINESCENCE OF POROUS SILICON [J].
FINKBEINER, S ;
WEBER, J .
THIN SOLID FILMS, 1995, 255 (1-2) :254-257
[5]   Classification and control of the origin of photoluminescence from Si nanocrystals [J].
Godefroo, S. ;
Hayne, M. ;
Jivanescu, M. ;
Stesmans, A. ;
Zacharias, M. ;
Lebedev, O. I. ;
Van Tendeloo, G. ;
Moshchalkov, V. V. .
NATURE NANOTECHNOLOGY, 2008, 3 (03) :174-178
[6]   The melting of silicon nanocrystals: Submicron thin-film structures derived from nanocrystal precursors [J].
Goldstein, AN .
APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, 1996, 62 (01) :33-37
[7]   Observation of monolayer-splitting for InAs/GaAs quantum dots [J].
Guffarth, F ;
Heitz, R ;
Schliwa, A ;
Pötschke, K ;
Bimberg, D .
PHYSICA E-LOW-DIMENSIONAL SYSTEMS & NANOSTRUCTURES, 2004, 21 (2-4) :326-330
[8]   Highly luminescent silicon nanocrystals with discrete optical transitions [J].
Holmes, JD ;
Ziegler, KJ ;
Doty, RC ;
Pell, LE ;
Johnston, KP ;
Korgel, BA .
JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 2001, 123 (16) :3743-3748
[9]   Control of thickness and orientation of solution-grown silicon nanowires [J].
Holmes, JD ;
Johnston, KP ;
Doty, RC ;
Korgel, BA .
SCIENCE, 2000, 287 (5457) :1471-1473
[10]   Second-harmonic generation from silicon nanocrystals embedded in SiO2 [J].
Jiang, Y ;
Wilson, PT ;
Downer, MC ;
White, CW ;
Withrow, SP .
APPLIED PHYSICS LETTERS, 2001, 78 (06) :766-768