Effect of oxygen pressure on structure and properties of Bi1.5Zn1.0Nb1.5O7 pyrochlore thin films prepared by pulsed laser deposition

被引：27

作者：

Zhang, Xiaohua ^{[1
]}

Ren, Wei ^{[1
]}

Shi, Peng ^{[1
]}

Chen, Xiaofeng ^{[1
]}

Wu, Xiaoqing ^{[1
]}

机构：

[1] Xi An Jiao Tong Univ, Key Lab, Minist Educ, Elect Mat Res Lab, Xian 710049, Peoples R China

来源：

APPLIED SURFACE SCIENCE | 2010年 / 256卷 / 06期

基金：

中国国家自然科学基金;

关键词：

BZN thin films; Pulsed laser deposition; Oxygen pressure; Dielectric properties; Tunability; DIELECTRIC-PROPERTIES; DEPENDENCE; ORIENTATION; THICKNESS;

D O I：

10.1016/j.apsusc.2009.10.020

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

The Bi2O3-ZnO-Nb2O5 (BZN) cubic pyrochlore thin films were prepared on Pt/TiO2/SiO2/Si(1 0 0) substrates by using pulsed laser deposition process. The oxygen pressure was varied in the range of 5-50 Pa to investigate its effect on the structure and dielectric properties of BZN thin films. It is found that oxygen pressure during deposition plays an important role on structure and other properties of BZN films. The BZN films deposited at temperature of 650 degrees C and at O-2 pressure of 5 Pa have an amorphous BZN and Nb2O5 phases but exhibits a cubic pyrochlore structure with a preferential (2 2 2) orientation when the oxygen pressure increases to 10 Pa. Dielectric constant and loss tangent of the films deposited at 10 Pa are 185 and 0.0008 at 10 kHz, respectively. The dielectric tunability is about 10% at a dc bias field of 0.9 MV/cm. (C) 2009 Elsevier B. V. All rights reserved.

引用

页码：1861 / 1866

页数：6

共 50 条

[21] Domain matched epitaxial growth of Bi1.5Zn1Nb1.5O7 thin films by pulsed laser deposition
Krishnaprasad, P. S.
Antony, Aldrin
Rojas, Fredy
Bertomeu, Joan
Jayaraj, M. K.
JOURNAL OF ALLOYS AND COMPOUNDS, 2014, 586 : 524 - 528
[22] Thickness-ratio-dependent dielectric properties of Bi1.5Zn1.0Nb1.5O7/Ba0.5Sr0.5TiO3 bilayered thin films
Li, Ruguan
Jiang, Shuwen
Gao, Libin
Li, Yanrong
MATERIALS SCIENCE AND ENGINEERING B-ADVANCED FUNCTIONAL SOLID-STATE MATERIALS, 2013, 178 (14): : 911 - 916
[23] High-K and low loss Bi1.5Zn1.0Nb1.5O7/polyimide composite films for application in embedded capacitors
Choi, Seung-Hoon
Kim, Il-Doo
Hong, Jae-Min
Oh, Seong-Guen
MACROMOLECULAR SYMPOSIA, 2007, 249 : 241 - 246
[24] Enhanced tunable and pyroelectric properties of Ba(Ti0.85Sn0.15)O3 thin films with Bi1.5Zn1.0Nb1.5O7 buffer layers
Wang, S. J.
Miao, S.
Reaney, I. M.
Lai, M. O.
Lu, L.
APPLIED PHYSICS LETTERS, 2010, 96 (08)
[25] Effect of annealing on crystallinity and electrical properties of Bi 1.5 MgNb 1.5 O 7 thin films
Zhang, Meixian
Xiang, Zhiqiang
Hong, Yingping
CERAMICS INTERNATIONAL, 2024, 50 (13) : 23451 - 23459
[26] Effects of substrate temperature on the dielectric properties of Bi1.5MgNb1.5O7 thin films derived from pulsed laser deposition
Yu, Shihui
Li, Lingxia
Zhang, Weifeng
Xu, Dan
Dong, Helei
Jin, Yuxin
MATERIALS CHEMISTRY AND PHYSICS, 2014, 148 (1-2) : 426 - 430
[27] Processing and Properties of Ba0.5Sr0.5TiO3/Bi1.5Zn1.0Nb1.5O7/Ba0.5Sr0.5TiO3 Sandwich Thin Films for Tunable Microwave Devices
Yan, Xin
Ren, Wei
Shi, Peng
Wu, Xiaoqing
Chen, Xiaofeng
Yao, Xi
FERROELECTRICS, 2010, 406 : 3 - 9
[28] The effect of Bi1.5Zn0.5Nb0.5Ti1.5O7 cover layer on the dielectric and tunable properties of Ba0.6Sr0.4TiO3/Bi1.5Zn0.5Nb0.5Ti1.5O7 bilayered thin films
Sun, Xiaohua
Yang, Ying
Zhang, Qiaoling
Luo, Zhimeng
Hou, Shuang
Huang, Caihua
Zou, Jun
MATERIALS SCIENCE AND ENGINEERING B-ADVANCED FUNCTIONAL SOLID-STATE MATERIALS, 2013, 178 (18): : 1244 - 1248
[29] Effect of external electric field on crystalline structure and dielectric properties of Bi1.5MgNb1.5O7 thin films*
Liu, Zhongzhe
Gao, Libin
Liang, Kexin
Fang, Zhen
Chen, Hongwei
Zhang, Jihua
CHINESE PHYSICS B, 2021, 30 (10)
[30] Microwave Properties of Bi1.5Zn1.0Nb1.5O7/Ba0.6Sr0.4TiO3 Hetero Layered Films Directly Sputtered on Si up to 50 GHz
Yang, Lihui
Wang, Genshui
Dong, Xianlin
Ponchel, Freddy
Remiens, Denis
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2011, 94 (08) : 2262 - 2265

← 1 2 3 4 5 →