Heat capacity measurement and EXAFS study of (U0.85Mg0.15)O-2-x for x=0 and 0.1

Heat capacities and electrical conductivities of (U-0.85 Mg-0.15)O2-x (x = 0 and 0.1) were measured simultaneously by means of a direct heating pulse calorimeter (DI-IPC) in the temperature range from 300 to 1500 K. Anomalous increases in the hear capacity curves of (U0.85Mg0.15)O2-x (x = 0 and 0.1) were observed above about 800 and 1150 K, respectively. The values for the enthalpy of oxygen Frenkel defect formation were calculated from the excess heat capacity and were found to be similar to those for UO2 doped with rare earth elements. On the other hand, no anomaly was seen in the electrical conductivity curve around the onset temperature of the anomalous increase in the heat capacity. It was, therefore, concluded that the excess hear capacity originates From the predominant contribution of the formation of Frenkel pair-like defects of oxygen. An extended X-ray absorption fine structure (EXAFS) experiment shows a different environment of oxygen around uranium and magnesium, and this should be a cause of the onset temperature difference.