Effect of Hydrothermal immersion and Hygrothermal Conditioning on Mechanical Properties of GRE Composite

Glass fibre reinforced epoxy (GRE) composite meet several degrading agents like moisture and temperature while its use in real time applications in civil infrastructures. Keeping this in mind, the short beam shear (SBS) specimens of GRE composite were exposed to such laboratory created stringent environment as a combination of moisture and elevated temperature for several periods. The environments are as: immersion in distilled water coupled with 65 degrees C as hydrothermal conditioning and an ambience containing 95% relative humidity at 60 degrees C as hygrothermal conditioning. Moisture treated SBS specimens were subjected to 3-point bend test to reveal inter laminar shear strength (ILSS), stress/strain at rupture and modulus values with periods of exposures. The concerned sample suffered 23% of degradation in ILSS values after 120 days of hydrothermal immersion and 25% after 90 days of hygrothermal conditioning. Samples at some optimum exposing conditions of both the exposures are thermally characterized by adopting differential scanning calorimetry (DSC) test. Glass transition temperature (T-g) of such representing samples were determined from the DSC thermograms. About 8 % reduction in T-g values was observed for the GRE composite sample, expectedly, due to moisture induced matrix plasticization and swelling. The fractographs as obtained through scanning electron microscope (SEM) revealed some causes of failures indicating the prime modes of failure of the treated GRE samples with optimum duration of both the exposures.