Ordering and orientation of CoPt/SiO2 granular films with additive Ag

被引：70

作者：

Chen, C ^{[1
]}

Kitakami, O ^{[1
]}

Okamoto, S ^{[1
]}

Shimada, Y ^{[1
]}

机构：

[1] Tohoku Univ, Sci Measurements Res Inst, Sendai, Miyagi 9808577, Japan

来源：

APPLIED PHYSICS LETTERS | 2000年 / 76卷 / 22期

关键词：

D O I：

10.1063/1.126634

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

We have studied the chemical ordering of granular films (CoPt)(1-x)Ag-x/SiO2 with the concentration x=2-6 at. %. It was found that the additive Ag efficiently promotes the ordering process, reducing the ordering temperature by 100 degrees C compared with that of without Ag. The additive Ag also stimulates nearly perfect (001) orientation of the CoPt-ordered grains in the films with a thickness of less than 50 nm, resulting in a large perpendicular magnetic anisotropy. (C) 2000 American Institute of Physics. [S0003- 6951(00)03322-2].

引用

页码：3218 / 3220

页数：3

共 14 条

[11] Perpendicular magnetic anisotropy and magnetic domain structure in sputtered epitaxial FePt (001) L10 films [J].

Thiele, JU ;

Folks, L ;

Toney, MF ;

Weller, DK .

JOURNAL OF APPLIED PHYSICS, 1998, 84 (10) :5686-5692

[12] DIRECT FORMATION OF ORDERED COPT AND FEPT COMPOUND THIN-FILMS BY SPUTTERING [J].

VISOKAY, MR ;

SINCLAIR, R .

APPLIED PHYSICS LETTERS, 1995, 66 (13) :1692-1694

[13]

Warren B.E., 1990, XRAY DIFFRACTION, P208

[14] MAGNETIC AND MAGNETOOPTICAL PROPERTIES OF COBALT-PLATINUM ALLOYS WITH PERPENDICULAR MAGNETIC-ANISOTROPY [J].

WELLER, D ;

BRANDLE, H ;

GORMAN, G ;

LIN, CJ ;

NOTARYS, H .

APPLIED PHYSICS LETTERS, 1992, 61 (22) :2726-2728

← 1 2 →