Lanthanum modification of crystalline phases and residual glass in augite glass ceramics produced with industrial solid wastes

被引:36
作者
Chen, Hua [1 ]
Li, Baowei [2 ]
Zhao, Ming [2 ]
Zhang, Xuefeng [1 ]
Du, Yongsheng [1 ]
Shi, Yu [2 ]
McCloy, John S. [3 ]
机构
[1] Inner Mongolia Univ Sci & Technol, Coll Sci, Baotou, Peoples R China
[2] Inner Mongolia Univ Sci & Technol, Key Lab Integrated Exploitat Bayan Obo Multimet R, Baotou, Peoples R China
[3] Washington State Univ, Sch Mech & Mat Engn, Pullman, WA 99164 USA
基金
中国国家自然科学基金;
关键词
Lanthanum oxide; Augite; Glass ceramics; Residual glass; Crystallization; PHOSPHATE-GLASSES; CR2O3; DIOPSIDE; LA2O3; BEHAVIOR; NUCLEATION; EVOLUTION;
D O I
10.1016/j.jnoncrysol.2019.119638
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
The effects of La2O3 on microstructure and properties of the CaO-MgO-SiO2-Al2O3 glass ceramics, made from Bayan Obo West Mine tailing and fly ash, were investigated. Results showed that 12203 additions up to 2 wt% promoted augite crystallization. Above this concentration, La2O3 suppressed augite crystallization by rather forming lanthanum oxyapatite that acted as a barrier for the growth of augite. Also Cr ions, the key element for the augite nuclei, were enriched in lanthanum oxyapatite. The La3+ cations were found to partially substitute for Ca2+ at the M2 structural sites in clinopyroxene (augite). Nano crystalline clusters, containing La3+, Na+, Ca2+, Mg2+ and Fe3+ in augite-like proportions, were found uniformly dispersed in the residual glassy phase. The glass ceramic with 2 wt% La2O3 shows optimum mechanical properties and chemical durability. The bending strength and Vickers hardness are 238 MPa and 7.57 GPa, acid and alkali-resistance are 97.5% and 98.9%, respectively.
引用
收藏
页数:10
相关论文
共 50 条
[1]   Effect of La2O3, CoO, Cr2O3 and MoO3 nucleating agents on crystallization behavior and magnetic properties of ferromagnetic glass-ceramic in the system Fe2O3•CaO•ZnO•SiO2 [J].
Abdel-Hameed, Salwa A. M. ;
Elwan, Rawhia. L. .
MATERIALS RESEARCH BULLETIN, 2012, 47 (05) :1233-1238
[2]   Structure of MoO3-WO3-La2O3-B2O3 glasses and crystallization of LaMo1 - xWxBO6 solid solutions [J].
Aleksandrov, Lyubomir ;
Komatsu, Takayuki ;
Shinozaki, Kenji ;
Honma, Tsuyoshi ;
Iordanova, Reni .
JOURNAL OF NON-CRYSTALLINE SOLIDS, 2015, 429 :171-177
[3]  
Barbieri L, 2000, J AM CERAM SOC, V83, P2515
[4]  
Chen H., 2015, J CHIN CERAM SOC, V43, P1101
[5]   La Doping Effect on the Dielectric Property of Barium Strontium Titanate Glass-Ceramics [J].
Chen, Jichun .
JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2014, 30 (03) :295-298
[6]   Effect of La2O3 on the physical and crystallization properties of Co2+-doped MgO-Al2O3-SiO2 glass [J].
Chen, Li ;
Yu, Chunlei ;
Hu, Lili ;
Chen, Wei .
JOURNAL OF NON-CRYSTALLINE SOLIDS, 2013, 360 :4-8
[7]   Pressure-induced preferential grain growth, texture development, and anisotropic properties of Fe/augite matrix composites prepared by spark plasma sintering [J].
Chen, W. L. ;
Zhang, X. F. ;
Jia, X. L. ;
Xu, W. C. ;
Liu, Y. L. ;
Li, B. W. .
MATERIALS RESEARCH EXPRESS, 2018, 5 (09)
[8]   Synthesis and characterization of iodosodalite [J].
Chong, Saehwa ;
Peterson, Jacob ;
Nam, Junghune ;
Riley, Brian ;
McCloy, John .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2017, 100 (05) :2273-2284
[9]  
El-Shennawi AWA, 1999, J AM CERAM SOC, V82, P1181
[10]  
ElMeliegy E, 2012, GLASSES AND GLASS CERAMICS FOR MEDICAL APPLICATIONS, P1, DOI 10.1007/978-1-4614-1228-1