Influence of dynamic annealing of irradiation defects on the deuterium retention behaviors in tungsten irradiated with neutron

被引：8
|
作者：
Kobayashi, Makoto [1 ]
Shimada, Masashi [2 ]
Taylor, Chase N. [2 ]
Buchenauer, Dean [3 ]
Kolasinski, Robert [3 ]
Koyanagi, Takaaki [4 ]
Nobuta, Yuji [5 ]
Hatano, Yuji [6 ]
Oya, Yasuhisa [7 ]
机构：
[1] Natl Inst Fus Sci, Natl Inst Nat Sci, 322-6 Oroshi, Toki, Gifu 5095202, Japan
[2] Idaho Natl Lab, Idaho Falls, ID USA
[3] Sandia Natl Labs, Albuquerque, NM USA
[4] Oak Ridge Natl Lab, Oak Ridge, TN USA
[5] Hokkaido Univ, Sapporo, Hokkaido, Japan
[6] Univ Toyama, Hydrogen Isotope Res Ctr, Toyama, Japan
[7] Shizuoka Univ, Shizuoka, Japan
来源：
FUSION ENGINEERING AND DESIGN | 2019年 / 146卷
关键词：
Tungsten; Neutron; Divertor; TDS; INDUCED DAMAGE; HYDROGEN; ENERGY;
D O I：
10.1016/j.fusengdes.2019.03.003
中图分类号：
TL [原子能技术]; O571 [原子核物理学];
学科分类号：
0827 ; 082701 ;
摘要：
Tungsten (W) samples were damaged by neutron and 6.4 MeV Fe-ion irradiation above 1000 K simulating the divertor operation temperature. Deuterium (D) retention properties were examined by decorating the damaged W with D and subsequent thermal desorption spectroscopy (TDS) measurements. Vacancy clusters were the major D trapping site in the W irradiated with Fe-ion at 873 K, although D retention by vacancy clusters decreased in the W irradiated with Fe-ion at 1173 K due to dynamic annealing. The D de-trapping activation energy from vacancy clusters was found to be 1.85 eV. D retention in neutron damage W was larger than that damaged by Fe-ion due to the uniform distribution of irradiation defects. The D desorption behaviors from neutron damaged W was simulated well by assuming the D de-trapping activation energy to be 1.52 eV.
引用
收藏
页码：1624 / 1627
页数：4
相关论文
共 50 条
  • [41] Comparison of dynamic deuterium retention in single-crystal and poly-crystals of tungsten: The role of natural defects
    Ghiorghiu, F.
    Minissale, M.
    Hodille, E. A.
    Grisolia, C.
    Angot, T.
    Bisson, R.
    NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS, 2019, 461 : 159 - 165
  • [42] The influence of displacement damage on deuterium retention in tungsten exposed to plasma
    Wampler, W. R.
    Doerner, R. P.
    NUCLEAR FUSION, 2009, 49 (11)
  • [43] Helium and Deuterium Retention in Plastically Deformed Tungsten under High-Flux Plasma Irradiation
    A. M. Bakaeva
    A. V. Bakaev
    D. A. Terentyev
    A. V. Dubinko
    E. E. Zhurkin
    Journal of Surface Investigation: X-ray, Synchrotron and Neutron Techniques, 2020, 14 : 1254 - 1259
  • [44] Defect evolution of neutron irradiated ITER grade tungsten after annealing
    Papadakis, D.
    Mergia, K.
    Manios, E.
    Chatzikos, V.
    Dellis, S.
    Terentyev, D.
    Bonny, G.
    Van Renterghem, W.
    Chang, C. C.
    Messoloras, S.
    FUSION ENGINEERING AND DESIGN, 2023, 189
  • [45] Helium and Deuterium Retention in Plastically Deformed Tungsten under High-Flux Plasma Irradiation
    Bakaeva, A. M.
    Bakaev, A., V
    Terentyev, D. A.
    Dubinko, A., V
    Zhurkin, E. E.
    JOURNAL OF SURFACE INVESTIGATION, 2020, 14 (06): : 1254 - 1259
  • [46] Kinetics of deuterium penetration into neutron-irradiated tungsten under exposure to high flux deuterium plasma
    Yajima, M.
    Hatano, Y.
    Ohno, N.
    Kuwabara, T.
    Toyama, T.
    Takagi, M.
    Suzuki, K.
    NUCLEAR MATERIALS AND ENERGY, 2019, 21
  • [47] Deuterium retention in displacement-damaged tungsten-rhenium alloys: Influence of rhenium concentration and irradiation temperature
    Zibrov, M.
    Cintora, A.
    Schwarz-Selinger, T.
    Hunger, K.
    Mayer, M.
    Bobyr, N. P.
    NUCLEAR MATERIALS AND ENERGY, 2024, 41
  • [48] Effect of noble gas ion pre-irradiation on deuterium retention in tungsten
    Cheng, L.
    Zhao, Z. H.
    De Temmerman, G.
    Yuan, Y.
    Morgan, T. W.
    Guo, L. P.
    Wang, B.
    Zhang, Y.
    Wang, B. Y.
    Zhang, P.
    Cao, X. Z.
    Lu, G. H.
    PHYSICA SCRIPTA, 2016, T167
  • [49] Influence of suppressed blistering by heavy ion pre-damage on deuterium retention in tungsten
    Wang, Ting
    Yuan, Yue
    Zhu, Xiu-Li
    Guo, Wangguo
    Zhu, Jipeng
    Wang, Shiwei
    Cheng, Long
    Lu, Guang-Hong
    NUCLEAR MATERIALS AND ENERGY, 2024, 41
  • [50] Influence of plasma heat loads relevant to ITER transient events on deuterium retention in tungsten
    Poskakalov, A. G.
    Gasparyan, Yu M.
    Efimov, V. S.
    Kovalenko, D. V.
    Barsuk, V. A.
    Klimov, N. S.
    Zibrov, M. S.
    Ogorodnikova, O. V.
    PHYSICA SCRIPTA, 2020, T171 (01)
12345