The effect of hot zone velocity and temperature gradient on the directional recrystallization of polycrystalline nickel

被引:31
作者
Li, J [1 ]
Johns, SL [1 ]
Iliescu, BM [1 ]
Frost, HJ [1 ]
Baker, I [1 ]
机构
[1] Dartmouth Coll, Thayer Sch Engn, Hanover, NH 03755 USA
基金
美国国家科学基金会;
关键词
directional recrystallization; columnar grains; hot zone velocity;
D O I
10.1016/S1359-6454(02)00265-3
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Cold-rolled polycrystalline nickel sheets were directionally annealed at 1000degreesC with either a large (1000degreesC/cm) or a small (50degreesC/cm) temperature gradient ahead of the hot zone. Columnar grains were produced at hot zone velocities from 2 to 100 mm/h for the large temperature gradient with only two similar to6 mm wide grains across the width at 5, 10 and 30 mm/h. With increasing hot zone velocity above 30 mm/h, the columnar grains became narrower. For the same range of hot zone velocities with a small temperature gradient, equiaxed grains were produced, with the grain size decreasing with increasing hot zone velocity. This difference arises because for the low temperature gradient recrystallization followed by substantial grain growth occurs ahead of the hot zone. Both interrupted directional annealing runs and runs (with the large temperature gradient) of nickel in which the nickel had been primary recrystallized at low temperature showed that the columnar grain structure developed by secondary recrystallization. (C) 2002 Acta Materialia Inc. Published by Elsevier Science Ltd. All rights reserved.
引用
收藏
页码:4491 / 4497
页数:7
相关论文
共 13 条
[1]  
Andrade ENDC, 1937, PROC R SOC LON SER-A, V163, P0016
[2]   Directional annealing of cold-rolled copper single crystals [J].
Baker, I ;
Li, J .
ACTA MATERIALIA, 2002, 50 (04) :805-813
[3]   DIRECTIONAL RECRYSTALLIZATION IN INCONEL MA 6000 NICKEL-BASE OXIDE DISPERSION STRENGTHENED SUPERALLOY [J].
BALOCH, MM ;
BHADESHIA, HKDH .
MATERIALS SCIENCE AND TECHNOLOGY, 1990, 6 (12) :1236-1246
[4]   CREEP-FATIGUE BEHAVIOR OF DIRECTIONALLY SOLIDIFIED AND SINGLE-CRYSTAL INTERMETALLIC NI3AL(B, HF) AT AN INTERMEDIATE TEMPERATURE [J].
BELLOWS, RS ;
SCHWARZKOPF, EA ;
TIEN, JK .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1988, 19 (03) :479-486
[5]   GRAIN-GROWTH IN DISPERSION STRENGTHENED SUPERALLOYS BY MOVING ZONE HEAT-TREATMENTS [J].
CAIRNS, RL ;
CURWICK, LR ;
BENJAMIN, JS .
METALLURGICAL TRANSACTIONS, 1975, 6 (01) :179-186
[6]  
Fujii T., 1984, Materials Letters, V2, P226, DOI 10.1016/0167-577X(84)90029-6
[7]   The effect of directional recrystallization on the low cycle fatigue response of a powder metallurgy nickel-based superalloy at elevated temperatures [J].
Godfrey, AW ;
Martin, JW .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1997, 222 (02) :91-100
[8]   EFFECT OF PROCESS VARIABLES ON THE STRUCTURE OF DIRECTIONALLY RECRYSTALLIZED MA-6000 [J].
HUMPHREYS, AO ;
SHAW, SWK ;
MARTIN, JW .
MATERIALS CHARACTERIZATION, 1995, 34 (01) :9-13
[9]  
MINO K, 1984, PM AEROSPACE MAT
[10]   On the secondary recrystallisation of Ma754 [J].
Miodownik, MA ;
Wilkinson, AJ ;
Martin, JW .
ACTA MATERIALIA, 1998, 46 (08) :2809-2821