Thermo-mechanical response of Al 6061 with and without equal channel angular pressing (ECAP)

The thermo-mechanical responses of Al 6061 before and after equal channel angular pressing (ECAP) at different strain rates and temperatures were measured. Al 6061 was solution heat treated before ECAP pressing at room temperature and subjected to up to three passes. After pressing, the billets were aged at 100 degrees C for 2 days. An as-received Al 6061-T651 was studied similarly to investigate the differences between processed and non-processed specimens. The responses of ECAP material were determined at -30, 22, 125 and 250 degrees C, and at strain rates from 10(-5) to 2530 s(-1): the 6061-T651 specimens were subjected to uniaxial compressive loading at -31, 22, 85,150, 230 and 315 degrees C, and strain rates ranging from 10(-5) to 2200 s(-1). It was found that, the ECAP process increases the strength versus the T651 condition. Additionally, the Al 6061 ECAP is not sensitive to strain rate at room and lower temperatures. but the sensitivity increases as the number of passes and/or temperature are increased and this is the same for the non-processed material. Increasing the number of passes increases the flow stress at room and lower temperatures, has almost no effect at 125 degrees C and decreases at 250 degrees C. For both materials. the dynamic flow stress is higher than the stress at quasi-static strain rates even when the quasi-static strain rate regime is insensitive to strain rate. The Al 6061 has strong texture after one pass but steadily increases as the number of passes are increased. This is the first study that reports on the thermo-mechanical responses of ECAP and non-ECAP Al 6061 at such a wide range of strain rates, including dynamic, and temperatures. (C) 2009 Elsevier Ltd. All rights reserved.