HF etching of CAD/CAM materials: influence of HF concentration and etching time on shear bond strength

Background The required pretreatment of CAD/CAM ceramic materials before resin composite cement application varies among studies. The aim of the present study was to evaluate the effect of hydrofluoric acid concentration and etching time on the shear bond strength (SBS) of two adhesive and two self-adhesive resin composite cements to different CAD/CAM ceramic materials. Methods SBS of two adhesive (Panavia V5, Kuraray, [PV5]; Vita Adiva F-Cem, Vita Zahnfabrik, [VAF]) and two self-adhesive (RelyX Unicem 2 Automix, 3 M Espe, [RUN]; Vita Adiva S-Cem, Vita, [VAS]) cements to four different CAD/CAM materials (Vitablocs Mark II, Vita, [VM]; Vita Enamic, Vita, [VE]; e.max CAD, Ivoclar Vivadent, [EC]; Vita Suprinity PC, Vita, [VS]) was measured. The effect of the surface pretreatment by using two different hydrofluoric acid products (HF5% Vita Ceramics Etch, Vita and HF9% buffered, Ultradent Porcelain Etch, Ultradent Products) were assessed at etching times of 0 s, 5 s, 15 s, 30s and 60s for each cement and restorative material combination (n = 10 per group, total n = 1440). Results Significant effects were found for the etching time and cement for all materials with highest shear bond strength for etching times of 60s = 30s = 15 s >= 5 s > 0 s and for RUN>PV5 = VAF > VAS (p < 0.05). Etching with HF5% for 5 s to 15 s resulted in higher SBS values, while no differences were observed between HF5% and HF9% buffered when the substrates were etched for 30s to 60s (p < 0.05). Conclusions Within the limitations of this study the recommended surface pretreatment of silicate ceramics is HF etching with concentrations of 5% or 9% for 15 s to 60s to achieve highest shear bond strength while the glassy matrix is sufficiently dissolved. The tested resin composite cements can be applied with all tested materials and suggested for clinical application.