Effect of refining processes on inclusions and mechanical properties of cast Al-2Li-2Cu-0.2Zr alloy

The effect of different refining processes on inclusions and mechanical properties of cast Al-2Li-2Cu-0.2Zr alloy was investigated, including two-stage hexachloroethane (C2Cl6) refining process, two-stage rotating gas bubbling refining process and two-stage composite refining process. It was found that the two-stage composite refining process, which combined C2Cl6 and rotating gas bubbling, can significantly improve the melt purity and mechanical properties of cast Al-2Li-2Cu-0.2Zr alloy. Compared to the unrefined alloy, the volume fraction of gas porosity defects and slag inclusions decreased from 1.47% to 0.12%, and the yield strength, ultimate tensile strength and elongation of as-quenched alloy increased from 113 MPa,179 MPa and 3.9% to 142 MPa, 293 MPa and 18.1%, respectively. C(2)Cl(6 )was first utilized to degas and remove large size slag inclusions before lithium addition, and then the rotating gas bubbling was utilized to do the further degassing and remove the suspended fine inclusions after lithium addition. The two-stage composite refining process can take advantage of two methods and get the remarkable refining effect.