Investigation of overheating of the final super-heater in a 660 MW power plant

被引：17

作者：

Liang, Zhiyuan ^{[1
]}

Jin, Xin ^{[1
]}

Zhao, Qinxin ^{[1
]}

机构：

[1] Xi An Jiao Tong Univ, Minist Educ, Key Lab Thermo Fluid Sci & Engn, Xian 710049, Peoples R China

来源：

ENGINEERING FAILURE ANALYSIS | 2014年 / 45卷

基金：

中国国家自然科学基金;

关键词：

Super-heater; Overheating; Steam oxidation; Exfoliation mechanism; OXIDE HYDROXIDE EVAPORATION; WATER-VAPOR; STEAM OXIDATION; ATMOSPHERES; BEHAVIOR; ALLOYS; STEELS; 304L;

D O I：

10.1016/j.engfailanal.2014.06.022

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Overheating of the final super-heater in a 660 MW power plant after service for 4700 h was investigated. The scanning electron microscopy (SEM) equipped with an energy dispersive spectrometer (EDS) was employed to observe the surface morphology and cross-section of the tube's steam side and analyze the ingredient of oxide scales. Results show that exfoliation of iron oxides was detected at the steam side of the tube, resulting in the over-heating of the final super-heater. Compressive stresses in the oxide scale generated during the unexpected shutdown of the power plant, which was responsible for the exfoliation of iron oxides. Finally, the growth and exfoliation mechanism of the oxide scale were put forward to conduct the related prevention and control measures. (C) 2014 Elsevier Ltd. All rights reserved.

引用

页码：59 / 64

页数：6

共 15 条

[1] Corrosion of nickel-chromium alloys, stainless steel and niobium at supercritical water oxidation conditions [J].

Asselin, Edouard ;

Alfantazi, Akram ;

Rogak, Steven .

CORROSION SCIENCE, 2010, 52 (01) :118-124

[2] Influence of water vapor and flow rate on the high-temperature oxidation of 304L; Effect of chromium oxide hydroxide evaporation [J].

Asteman, H ;

Svensson, JE ;

Norell, M ;

Johansson, LG .

OXIDATION OF METALS, 2000, 54 (1-2) :11-26

[3] Indication of chromium oxide hydroxide evaporation during oxidation of 304L at 873 K in the presence of 10% water vapor [J].

Asteman, H ;

Svensson, JE ;

Johansson, LG ;

Norell, M .

OXIDATION OF METALS, 1999, 52 (1-2) :95-111

[4] Enhanced oxidation of the 9%Cr steel P91 in water vapour containing environments [J].

Ehlers, J. ;

Young, D. J. ;

Smaardijk, E. J. ;

Tyagi, A. K. ;

Penkalla, H. J. ;

Singheiser, L. ;

Quadakkers, W. J. .

CORROSION SCIENCE, 2006, 48 (11) :3428-3454

[5] Mechanisms of steam oxidation in high strength martensitic steels [J].

Ennis, P. J. ;

Quadakkers, W. J. .

INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2007, 84 (1-2) :75-81

[6]

Fry A., 2002, OXIDATION ALLOYS STE

[7] Microstructural investigation of the oxide formed on TP 347H FG during long-term steam oxidation [J].

Hansson, A. N. ;

Danielsen, H. ;

Grumsen, F. B. ;

Montgomery, M. .

MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2010, 61 (08) :665-675

[8] Microstructure Evolution During Steam Oxidation of a Nb Stabilized Austenitic Stainless Steel [J].

Hansson, A. N. ;

Pantleon, K. ;

Grumsen, F. B. ;

Somers, M. A. J. .

OXIDATION OF METALS, 2010, 73 (1-2) :289-309

[9] Study of the corrosion behavior of a 18Cr-oxide dispersion strengthened steel in supercritical water [J].

Hu, Helong ;

Zhou, Zhangjian ;

Li, Ming ;

Zhang, Lefu ;

Wang, Man ;

Li, Shaofu ;

Ge, Changchun .

CORROSION SCIENCE, 2012, 65 :209-213

[10] History of power plants and progress in heat resistant steels [J].

Masuyama, F .

ISIJ INTERNATIONAL, 2001, 41 (06) :612-625

← 1 2 →