Study on acrylic emulsion adhesive modified by double siloxane

被引：0
|
作者：
Gao, Caihua [1 ]
Guo, Wenlu [1 ]
Jin, Zhiming [1 ]
机构：
[1] Jiangsu Univ Sci & Technol, Sch Biol & Chem Engn, Zhenjiang 212003, Jiangsu, Peoples R China
来源：
ADVANCED MATERIALS AND PROCESSES III, PTS 1 AND 2 | 2013年 / 395-396卷
关键词：
acrylic adhesive; modification; double siloxane;
D O I：
10.4028/www.scientific.net/AMM.395-396.367
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The acrylic emulsion adhesive was modified by D4 and KH570 with chemical process, and we can get the modified product successfully via the best technology parameter which was confirmed by orthogonal experiment. The structure of acrylic was characterized by FTIR., while there was a comparative study on the macroscopic properties and thermal stability of the unmodified and modified product. The results showed that when m(D4):m(KH570) was 2:1, the dosage of emulsifier was 3.0%, the dosage of KPS was 4.0%, the monomer(soft and hard) ratio was 1:1, the stability of the acrylic emulsion adhesive modified by double siloxane was good, and its viscosity, water resistance, heat resistance were improved greatly.
引用
收藏
页码：367 / 370
页数：4
相关论文
共 50 条
  • [21] Synthesis and properties of the organosilicon modified acrylic/LDH nanocomposite emulsion
    Department of Applied Chemistry, School of Science, Northwestern Polytechnical University, Xi'an 710072, China
    Gaofenzi Cailiao Kexue Yu Gongcheng/Polymeric Materials Science and Engineering, 2008, 24 (10): : 45 - 48
  • [22] Structure and adhesive properties of epoxy resins modified with acrylic particles
    Ashida, T
    Ochi, M
    JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 1997, 11 (04) : 519 - 530
  • [23] Structure and adhesive properties of epoxy resins modified with acrylic particles
    Ashida, Tadashi
    Ochi, Mitsukazu
    Journal of Adhesion Science and Technology, 1997, 11 (04): : 519 - 530
  • [24] Enhanced Stability of the Dispersed Phase Stabilized by Polyether-Modified Siloxane in the Double Emulsion System: Storage Stability and Rheological Investigation
    Debeli, Dereje Kebebew
    Lin, Chao
    Gan, Liang
    Deng, Jianjun
    Hu, Liuyun
    Shan, Guorong
    INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH, 2020, 59 (20) : 9688 - 9698
  • [25] Study on the Effect of Acrylic Acid Emulsion on the Properties of Poplar Wood Modified by Sodium Silicate Impregnation
    Zhang, Yuan
    Guan, Pengfei
    Ma, Xin
    Li, Ping
    Sun, Zhenyu
    Li, Xianjun
    Zuo, Yingfeng
    FORESTS, 2023, 14 (06):
  • [26] Study of acrylic inverse-emulsion copolymerization
    Tsinghua Univ, Beijing, China
    Qinghua Daxue Xuebao, 6 (49-51, 55):
  • [27] Effect of network morphology on adhesive performance in emulsion blends of acrylic pressure sensitive adhesives
    Tobing, Singa
    Klein, Andrew
    Sperling, L.H.
    Petrasko, Bob
    2001, John Wiley and Sons Inc. (81)
  • [28] Effect of network morphology on adhesive performance in emulsion blends of acrylic pressure sensitive adhesives
    Tobing, S
    Klein, A
    Sperling, LH
    Petrasko, B
    JOURNAL OF APPLIED POLYMER SCIENCE, 2001, 81 (09) : 2109 - 2117
  • [29] Energy dissipation and adhesive failure of acrylic emulsion-based pressure sensitive adhesives
    Wang, Qifeng
    Griffith, William
    Einsla, Melinda
    Nedwick, Paul
    Pacholski, Michaeleen
    Zhang, Sipei
    Shull, Kenneth
    ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 2016, 252
  • [30] Properties of Acrylic Emulsion Modified Magnesium Oxychloride Cement and Its Mechanism
    Li, Xiaoqing
    Bian, Libo
    Ding, Linna
    Zhang, Lu
    Wei, Xia
    Jianzhu Cailiao Xuebao/Journal of Building Materials, 2024, 27 (06): : 479 - 486
12345