Development of Nb3Al superconducting wire for accelerator magnets

被引：14

作者：

Kobayashi, T ^{[1
]}

Tsuchiya, K

Shintomi, T

Terashima, A

Banno, N

Nimori, S

Takeuchi, T

Tagawa, K

Iwaki, G

机构：

[1] KEK, High Energy Accelerator Res Org, Tsukuba, Ibaraki 3050801, Japan

[2] Natl Inst Mat Sci, Tsukuba, Ibaraki 3050003, Japan

[3] Hitachi Cable Ltd, Tsuchiura, Ibaraki 3000026, Japan

来源：

IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY | 2004年 / 14卷 / 02期

关键词：

accelerator magnets; critical current density; Nb3Al wire; rapid-heating/quenching process;

D O I：

10.1109/TASC.2004.830370

中图分类号：

TM [电工技术]; TN [电子技术、通信技术];

学科分类号：

0808 ; 0809 ;

摘要：

Nb3Al superconductors have shown promising performance compared to Nb3Sn conductors when processed by rapid heating/quenching process. Therefore we have started an R&D program of Nb3Al conductors for future accelerator magnets. Several test wires of around 0.8 mm diameter, which have relatively small filament (similar to50 micron diameter) and low matrix ratio (similar to1.0), were fabricated, and the heat treatment and area reduction conditions after the rapid quenching process were studied. The highest noncopper J(c) achieved during this study was 1734 A/mm(2) at 10 T and 4.2

引用

页码：1016 / 1019

页数：4

共 7 条

[1] CRITICAL-CURRENT DEGRADATION IN MULTIFILAMENTARY Nb3Al WIRES FROM TRANSVERSE COMPRESSIVE AND AXIAL TENSILE STRESS [J].

Bray, S. L. ;

Ekin, J. W. ;

Kuroda, T. .

IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 1993, 3 (01) :1338-1341

[2]

EVANS L, STATUS LHC

[3]

SCANLAN RM, 2002, ADV CRYOGENIC ENG B, V48, P949

[4] Nb3Al conductors for high-field applications [J].

Takeuchi, T .

SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2000, 13 (09) :R101-R119

[5] Nb3Al superconductors [J].

Takeuchi, T .

IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2002, 12 (01) :1088-1093

[6]

TAYLOR TM, 2002, P 8 EUR PART ACC C E, P129

[7]

Tsuchiya K., 2002, P 9 INT CRYO ENG C G, P633

← 1 →