Tensile fracture behavior of notched 9Cr-1Mo ferritic-martensitic steel specimens in contact with liquid lead-bismuth eutectic at 350 °C

被引：16
作者：
Gong, Xing [1 ,2 ]
Stergar, Erich [2 ]
Marmy, Pierre [2 ]
Gavrilov, Serguei [2 ]
机构：
[1] China Nucl Power Technol Res Inst Co Ltd, China Gen Nucl Power Corp CGN, Nucl Fuel Res & Dev Ctr, Dept ATF R&D, Shenzhen 518026, Peoples R China
[2] SCK CEN, Belgian Nucl Res Ctr, Boeretang 200, B-2400 Mol, Belgium
来源：
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2017年 / 692卷
关键词：
T91; LBE; LME; Fracture; LOW-CYCLE FATIGUE; METAL EMBRITTLEMENT; STRAIN-RATE; MECHANICAL-PROPERTIES; CRACK PROPAGATION; T91; STEEL; LBE; SUSCEPTIBILITY; TESTS; TEMPERATURE;
D O I：
10.1016/j.msea.2017.03.067
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Cracking jumps were observed in notched T91 (9Cr-1Mo ferritic-martensitic steel) specimens tested in liquid lead-bismuth eutectic (LBE) at 350 degrees C under tensile loading. The cracking jumps manifested themselves as being regular steps at tensile curves, while as being fatigue striation-like markings at fracture surfaces. The markings were consisted of liquid metal embrittlement (LME) zones and ductile zones. The liquid LBE was adsorbed at crack tip and likely reduced the interatomic bonding strength, leading to cracking in a brittle way and release of elastic energy in the load line. This unique phenomenon was found to be associated with coupled effects of LME and compliance/stiffness of tensile machines.
引用
收藏
页码：139 / 145
页数：7
相关论文
共 24 条
[1]   Effect of contact conditions on embrittlement of T91 steel by lead-bismuth [J].
Auger, T ;
Lorang, G ;
Guérin, S ;
Pastol, JL ;
Gorse, D .
JOURNAL OF NUCLEAR MATERIALS, 2004, 335 (02) :227-231
[2]   Slow strain rate tensile tests on T91 in static lead-bismuth eutectic [J].
Dai, Y. ;
Long, B. ;
Groeschel, F. .
JOURNAL OF NUCLEAR MATERIALS, 2006, 356 (1-3) :222-228
[3]   Investigating liquid-metal embrittlement of T91 steel by fracture toughness tests [J].
Ersoy, Feyzan ;
Gavrilov, Serguei ;
Verbeken, Kim .
JOURNAL OF NUCLEAR MATERIALS, 2016, 472 :171-177
[4]  
Fernandes PJL, 1997, INT MATER REV, V42, P251, DOI 10.1179/095066097790093163
[5]   Opportunities for the LWR ATF materials development program to contribute to the LBE-cooled ADS materials qualification program [J].
Gong, Xing ;
Li, Rui ;
Sun, Maozhou ;
Ren, Qisen ;
Liu, Tong ;
Short, Michael P. .
JOURNAL OF NUCLEAR MATERIALS, 2016, 482 :218-228
[6]   Temperature dependence of liquid metal embrittlement susceptibility of a modified 9Cr-1Mo steel under low cycle fatigue in lead-bismuth eutectic at 160-450 °C [J].
Gong, Xing ;
Marmy, Pierre ;
Qin, Ling ;
Verlinden, Bert ;
Wevers, Martine ;
Seefeldt, Marc .
JOURNAL OF NUCLEAR MATERIALS, 2016, 468 :289-298
[7]   Multiscale investigation of quasi-brittle fracture characteristics in a 9Cr-lMo ferritic-martensitic steel embrittled by liquid lead-bismuth under low cycle fatigue [J].
Gong, Xing ;
Marmy, Pierre ;
Volodin, Alexander ;
Amin-Ahmadi, Behnam ;
Qin, Ling ;
Schryvers, Dominique ;
Gavrilov, Serguei ;
Stergar, Erich ;
Verlinden, Bert ;
Wevers, Martine ;
Seefeldt, Marc .
CORROSION SCIENCE, 2016, 102 :137-152
[8]   Low cycle fatigue behavior of a modified 9Cr-1Mo ferritic-martensitic steel in lead-bismuth eutectic at 350 °C - Effects of oxygen concentration in the liquid metal and strain rate [J].
Gong, Xing ;
Marmy, Pierre ;
Verlinden, Bert ;
Wevers, Martine ;
Seefeldt, Marc .
CORROSION SCIENCE, 2015, 94 :377-391
[9]   Effect of liquid metal embrittlement on low cycle fatigue properties and fatigue crack propagation behavior of a modified 9Cr-1Mo ferritic-martensitic steel in an oxygen-controlled lead-bismuth eutectic environment at 350 °C [J].
Gong, Xing ;
Marmy, Pierre ;
Qin, Ling ;
Verlinden, Bert ;
Wevers, Martine ;
Seefeldt, Marc .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 618 :406-415
[10]  
Hamouche-Hadjem Z., 2009, CORROS SCI, V51, P2580
123