The temperature behavior of smart windows under direct solar radiation

The purpose of this paper was to investigate the variation in temperature of electrochromic devices under direct solar radiation and to compare the results with double-glazed glass. The devices consisted of a V(2)O(5) layer as an ion storage film and a WO(3) layer as an electrochromic layer. The V(2)O(5) and WO(3) films were prepared by thermal and electron beam evaporation, respectively. The optical properties and structures of these films were investigated. Both the ion storage film and the electrochromic layer were amorphous. The optical absorption was caused by a direct-forbidden transition in V(2)O(5) and by an indirect-allowed transition in WO(3). The maximum temperatures under solar radiation were measured for colored and bleached devices, double glass and air, they were found to be approximately 63, 63, 53 and 36 degrees C, respectively. The rates of increasing temperature to the incident power density for colored, bleached devices and double glass were 0.051, 0.049 and 0.041 degrees C/(W/m(2)). respectively. (C) 2009 Elsevier B V. All rights reserved