Characteristics of the Sierra Leone High Alumina Iron Ore and Utilization in Sintering

被引:4
作者
Dong Jie-ji [1 ,2 ]
Wang Guang [1 ,3 ]
Zuo Mao-fang [2 ]
Li Hua [2 ]
Xue Qing-guo [1 ,3 ]
机构
[1] Univ Sci & Technol Beijing, State Key Lab Adv Met, Beijing 100083, Peoples R China
[2] Zhang Dian Steel Plant, Zibo 256400, Peoples R China
[3] Univ Sci & Technol Beijing, State Key Lab Adv Met, Beijing 100083, Peoples R China
来源
CHEMICAL, MATERIAL AND METALLURGICAL ENGINEERING III, PTS 1-3 | 2014年 / 881-883卷
关键词
Sierra Leone iron ore; sintering; characteristics; TG-DSC; gibbsite; GIBBSITE;
D O I
10.4028/www.scientific.net/AMR.881-883.1515
中图分类号
TQ [化学工业];
学科分类号
0817 ;
摘要
The characteristics of the Sierra Leone iron ore were studied at laboratory scale by chemical analysis, XRD, SEM-EDS and TG-DSC methods. The Sierra Leone iron ore was a kind of limonite, which was mainly consisted of hematite, goethite and gibbsite. The iron ore lost its crystal water at a fast speed ranging from 200 degrees C to 400 degrees C and the total content of the crystal water was about 8.2 wt.%. The initial melt formation temperature of the iron ore with CaO was stably kept at around 1209 C and the amount of liquid increased with the increasing of CaO content. Its melt formation temperature is higher than Australian limonite. The sintering pot test showed that the yield of sinter decreases from 78.37wt.% to 73.36wt.% and the drum index decreases from 60.5wt.% to 49.63wt.% when the blending ratio of Sierra Leone iron ore increases from 7wt.% to 27.3wt.%.
引用
收藏
页码:1515 / +
页数:2
相关论文
共 9 条
[1]  
[Anonymous], 1995, VDEH SLAG ATL, P58
[2]  
[郭兴敏 Guo Xingmin], 2004, [钢铁, Iron and Steel], V39, P34
[3]   Differential thermal analysis of assimilation and melt-formation phenomena in the sintering process of iron ores [J].
Kasai, E ;
Saito, F .
ISIJ INTERNATIONAL, 1996, 36 (08) :1109-1111
[4]  
[李金莲 LI Jinlian], 2011, [钢铁, Iron and Steel], V46, P19
[5]   Factors influencing the bonding phase structure of iron ore sinters [J].
Loo, CE ;
Leung, W .
ISIJ INTERNATIONAL, 2003, 43 (09) :1393-1402
[6]   Effects of alumina on sintering performance of hematite iron ores [J].
Lu, L. ;
Holmes, R. J. ;
Manuel, J. R. .
ISIJ INTERNATIONAL, 2007, 47 (03) :349-358
[7]   Thermal decomposition of mechanically activated gibbsite [J].
MacKenzie, KJD ;
Temuujin, J ;
Okada, K .
THERMOCHIMICA ACTA, 1999, 327 (1-2) :103-108
[8]   Reaction sequences in the formation of silico-ferrites of calcium and aluminum in iron ore sinter [J].
Scarlett, NVY ;
Pownceby, MI ;
Madsen, IC ;
Christensen, AN .
METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2004, 35 (05) :929-936
[9]   EFFECT OF GIBBSITE ON SINTERING PROPERTY AND SINTER QUALITY [J].
YAMAOKA, Y ;
NAGAOKA, S ;
YAMADA, Y ;
ANDO, R .
TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1974, 14 (03) :185-194