Effect of the composition and concentration of fibrous wastes from linen yarn production on the physicomechanical properties of polyolefin composites

被引:10
作者
Kayaks, YA [1 ]
Bulmanis, BN [1 ]
Reikhmane, SA [1 ]
Tsiprin, MG [1 ]
机构
[1] LATVIAN ACAD SCI,INST POLYMER MECH,LV-1006 RIGA,LATVIA
关键词
D O I
10.1007/BF02256088
中图分类号
O3 [力学];
学科分类号
08 ; 0801 ;
摘要
An analysis is made of the feasibility of using wastes from the production of linen yarn (scutch, spinning and carding refuse) to modify low-density polyethylene. The effect of the composition and concentration of wastes on the processing properties (melt index), physicomechanical indices (tensile strength, elastic modulus in bending), and water resistance of composites based on low-density polyethylene is studied. It is found that the melt index decreases with an increase in the content of filler and that even a composite with a high filler content (40-50% by weight) maintains values of 0.2-0.3 g/10 min. The elastic modulus in bending increases with an increase in the content of waste, regardless of the nature of the latter. Tensile strength increases slightly and depends on the choice of filler. This result, combined with the reduction in the scatter of values of elastic madulus with an increase in filler concentration, is an indicator of the relatively high degree of heterogeneity of the systems that were studied. The water resistance of the composites decreases with an increase in filler content. To reduce the heterogeneity of the systems, mixing should be intensified and modifiers such as stearic acid and polyisocyanates should be added.
引用
收藏
页码:293 / 298
页数:6
相关论文
共 20 条
[1]  
CARLOS ACR, 1986, NATURAL FIBER REINFO, P110
[2]  
CLAROU C, 1984, INT J POLYM SCI, V10, P159
[3]  
GATENHOLM P, 1995, EFFECT SURFACE INDUC
[4]  
JAM KL, 1990, POLYM ENG SCI, V30, P693
[5]  
JAYMOL G, 1995, J APPL POLYM SCI, V57, P843
[6]   PROCESSING AND CHARACTERIZATION OF JUTE FIBER REINFORCED THERMOPLASTIC POLYMERS [J].
KARMAKER, AC ;
HINRICHSEN, G .
POLYMER-PLASTICS TECHNOLOGY AND ENGINEERING, 1991, 30 (5-6) :609-629
[7]  
KUKHAREV MS, 1993, TEKST PROM, P23
[8]  
Manson J, 1979, POLYM MIXTURES COMPO
[9]  
MITCHELL AJ, 1984, APPITA, V31, P347
[10]  
PADILLA A, 1984, J APPL POLYM SCI, V29, P2405