Wear and fracture toughness of partially stabilized zirconia ceramics under dry friction against steel

被引：5

作者：

Akimov, G. Ya. ^{[1
]}

Chaika, E. V. ^{[1
]}

Marinin, G. A. ^{[1
]}

机构：

[1] Natl Acad Sci Ukraine, Galkin Donetsk Physicotech Inst, UA-83114 Donetsk, Ukraine

来源：

JOURNAL OF FRICTION AND WEAR | 2009年 / 30卷 / 02期

关键词：

zirconia; wear; fracture toughness; phase transformations; isostatic pressing;

D O I：

10.3103/S1068366609020019

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

The wear of two ceramic materials containing partially stabilized zirconia is studied under unlubricated friction against steel. The first material, with ZrO2 and 3 mol % Y2O3, was obtained by cold isostatic pressing and sintering. The second material, comprising ZrO2 and 4 mol % Y2O3, was fabricated by additional hot isostatic pressing. The samples of both materials were fabricated with high and low values of fracture toughness. The samples with high fracture toughness are found to wear more intensively. This fact can be explained by surface micro-cracking during braking as a result of phase transformations.

引用

页码：77 / 79

页数：3

共 13 条

[1]

AKIMOV GY, 2007, ZH TEKH FIZ, V77, P114

[2]

AKIMOV GY, 2003, REFRACT IND CERAM, P2

[3]

AKIMOV GY, 2006, PISMA ZH TEKH FIZ, V32, P49

[4] Toughening of yttria-stabilised tetragonal zirconia ceramics [J].

Basu, B .

INTERNATIONAL MATERIALS REVIEWS, 2005, 50 (04) :239-256

[5] Microstructure-toughness-wear relationship of tetragonal zirconia ceramics [J].

Basu, B ;

Vleugels, J ;

Van Der Blest, O .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2004, 24 (07) :2031-2040

[6]

CHAIKA EV, 2005, REFRACT IND CERAM, P10

[7]

*GOST, 945076 GOST

[8]

Kragelskii I.V., 1968, Friction and Wear

[9]

MIYOSHI T, 1985, T JPN SOC MECH ENG A, V51, P2487

[10]

[РУБЦОВ В.Е. Rubtsov V.E.], 2007, [Трение и износ, Trenie i iznos], V28, P169

← 1 2 →