Hot-Corrosion Behavior of Modified YSZ Thermal Barrier Coating

被引：1

作者：

Wang, Yi ^{[1
]}

Chen, Lijia ^{[1
]}

Suo, Hongli ^{[1
]}

Meng, Yichen ^{[1
]}

机构：

[1] Beijing Univ Technol, Coll Mat Sci & Engn, Minist Educ, Key Lab Adv Funct Mat, Beijing 100124, Peoples R China

来源：

POWER AND ENERGY SYSTEMS III | 2014年 / 492卷

关键词：

hot-corrosion; superalloy; plasma-spraying; cracks;

D O I：

10.4028/www.scientific.net/AMM.492.361

中图分类号：

TE [石油、天然气工业]; TK [能源与动力工程];

学科分类号：

0807 ; 0820 ;

摘要：

A modified YSZ thermal barrier coating (TBC) was prepared by simultaneously depositing two components, NiCrAlY and YSZ, on nicked-based superalloy DZ125 via atmospheric plasma spraying. In this study, the sodium salt was deposited on substrate surface at the deposition rate of 3 mg/cm(-2). After being heated at 950 degrees C for 50min, the specimens were cooled to ambient temperature within 10 min. The specimens were recoated after each 10 cycles. Subsequently, the corrosion products were analyzed via X-Ray diffraction and SEM. The results indicated that deterioration of traditional YSZ coating mainly resulted from the fluxing of thermal grown oxides (TGO). Conversely, abnormal growth of TGO and enrichment of molten salt around segmentation crack were not observed in the modified YSZ thermal barrier coating. Moreover, the modified YSZ-TBC exhibited higher thermal resistance than traditional YSZ-TBC in the thermal cycling testing.

引用

页码：361 / 364

页数：4

共 8 条

[1]

Cernaschi F., 1997, J THERM SPRAY TECHN, V6, P35

[2]

Dong H.Y., 2010, SURF COAT TECHNOL, V204, P3366

[3] Lanthanum hexaaluminate - novel thermal barrier coatings for gas turbine applications - materials and process development [J].

Gadow, R ;

Lischka, M .

SURFACE & COATINGS TECHNOLOGY, 2002, 151 :392-399

[4] Effect of hollow spherical powder size distribution on porosity and segmentation cracks in thermal barrier coatings [J].

Guo, H. B. ;

Murakami, H. ;

Kuroda, S. .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2006, 89 (12) :3797-3804

[5] Thermo-Physical Properties and Thermal Shock Resistance of Segmented La2Ce2O7/YSZ Thermal Barrier Coatings [J].

Guo, Hongbo ;

Wang, Yi ;

Wang, Lu ;

Gong, Shengkai .

JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2009, 18 (04) :665-671

[6] High temperature corrosion behaviour of a gradient NiCoCrAlYSi coating II: Oxidation and hot corrosion [J].

Jiang, S. M. ;

Li, H. Q. ;

Ma, J. ;

Xu, C. Z. ;

Gong, J. ;

Sun, C. .

CORROSION SCIENCE, 2010, 52 (07) :2316-2322

[7] Segmented lanthanum cerium oxide thermal barrier coatings by atmospheric plasma spray [J].

Wang, Y. ;

Guo, H. B. ;

Li, Z. Y. ;

Gong, S. K. .

SURFACE ENGINEERING, 2009, 25 (07) :555-558

[8] Thermal shock resistance and mechanical properties of La2Ce2O7 thermal barrier coatings with segmented structure [J].

Wang, Yi ;

Guo, Hongbo ;

Gong, Shengkai .

CERAMICS INTERNATIONAL, 2009, 35 (07) :2639-2644

← 1 →