Vertical continuous compound casting of copper aluminum bilayer rods

被引：11

作者：

Gress, Thomas ^{[1
]}

Nardi, Vanessa Glueck ^{[2
]}

Schmid, Simon ^{[1
]}

Hoyer, Julika ^{[1
]}

Rizaiev, Yevgen ^{[1
]}

Boll, Torben ^{[3
,4
]}

Seils, Sascha ^{[3
,4
]}

Tonn, Babette ^{[2
]}

Volk, Wolfram ^{[1
]}

机构：

[1] Tech Univ Munich TUM, Chair Met Forming & Casting, Walther Meissner Str 4, D-85748 Garching, Germany

[2] Tech Univ Clausthal, Inst Met, Robert Koch Str 42, D-38678 Clausthal Zellerfeld, Germany

[3] Karlsruhe Inst Technol KIT, Inst Appl Mat IAM, Engelbert Arnold Str 4, D-76131 Karlsruhe, Germany

[4] Karlsruhe Inst Technol KIT, Karlsruhe Nano Micro Facil KNMF, Hermann von Helmholtz Pl 1, D-76344 Eggenstein Leopoldshafen, Germany

来源：

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY | 2021年 / 288卷

关键词：

Continuous compound casting; Cohesion; Bimetal; Casting simulation; Interface development; Copper aluminum composite; BIMETALLIC CASTINGS; COLD EXTRUSION; CLAD COMPOSITE; INTERFACE; MICROSTRUCTURE; TOMOGRAPHY; HEAT;

D O I：

10.1016/j.jmatprotec.2020.116854

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

A vertical continuous compound casting technology for the production of rotationally symmetric bilayer rods consisting of brass CuZn37 and aluminum AA7075 was developed. The interface of the metallurgically bonded semi-finished products was composed of four intermetallic layers and an anomalous eutectic area of Al2Cu (theta-AlCu), Al solid solution (alpha-Al), and other intermetallic precipitates. The intermetallic layers were CuZn (beta-CuZn), a suggested two-phase region of Al3Cu5Zn2 (tau-AlCuZn) and Cu5Zn8 (gamma-CuZn), Al4Cu3Zn (tau'-AlCuZn), and AlCu (eta(2)-AlCu). The correlation between the process parameters casting speed, cladding temperature, and tool tempering and the interface formation was studied. The experimental investigations were accompanied by a numerical FEM analysis. The casting speed and the cladding temperature were found to be key factors, that influence the formation of a cohesion between the joining partners.

引用

页数：16

共 43 条

[1] ON THE INTERFACIAL CHARACTERISTICS OF COMPOUND CAST Al/BRASS BIMETALS
Akbarifar, Mehdi
Divandari, Mehdi
[J]. INTERNATIONAL JOURNAL OF METALCASTING, 2017, 11 (03) : 506 - 512
[2] Anderson M.D., 2005, Patent, Patent No. [US 2005/0011630 Al, 0011632]
[3] [Anonymous], 2009, ARCH MAT SCI ENG
[4] [Anonymous], 1998, THESIS
[5] Bogno A.-A., 2019, MATER SCI ENG, V529, P1
[6] Stability of Hume-Rothery phases in Cu-Zn alloys at pressures up to 50 GPa
Degtyareva, VF
Degtyareva, O
Sakharov, MK
Novokhatskaya, NI
Dera, P
Mao, HK
Hemley, RJ
[J]. JOURNAL OF PHYSICS-CONDENSED MATTER, 2005, 17 (50) : 7955 - 7962
[7] Study of Al/Cu rich phases formed in A356 alloy by inserting Cu wire in pattern in LFC process
Divandari, M.
Golpayegani, A. R. Vahid
[J]. MATERIALS & DESIGN, 2009, 30 (08): : 3279 - 3285
[8] Metallurgical process analysis and microstructure characterization of the bonding interface of QAl9-4 aluminum bronze and 304 stainless steel composite materials
Dong, Longlong
Chen, Wenge
Hou, Lintao
Liu, Yingbin
Luo, Qiwen
[J]. JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2016, 238 : 325 - 332
[9] Eckerlin P., 1971, CONDENS MATTER
[10] Friedel A., 1995, GIESSEREI, V23, P442

← 1 2 3 4 5 →