Quantitative measurements of dynamic precipitation during fatigue of an Al-Zn-Mg-(Cu) alloy using small-angle X-ray scattering

被引:102
作者
Hutchinson, C. R. [1 ]
de Geuser, F. [2 ,3 ]
Chen, Y. [1 ,4 ]
Deschamps, A. [2 ,3 ]
机构
[1] Monash Univ, Dept Mat Engn, ARC Ctr Excellence Design Light Met, Clayton, Vic 3168, Australia
[2] Univ Grenoble Alpes, SIMAP, F-38000 Grenoble, France
[3] CNRS, SIMAP, F-38000 Grenoble, France
[4] Monash Univ, Monash Ctr Electron Microscopy, Clayton, Vic 3168, Australia
基金
澳大利亚研究理事会; 欧洲研究理事会;
关键词
Dynamic precipitation; Cyclic deformation; Fatigue; 7xxx; Small-angle X-ray scattering; ZN-MG ALLOY; PERSISTENT SLIP BANDS; CYCLIC DEFORMATION; PLASTIC-DEFORMATION; VOLUME FRACTION; ATOM-PROBE; ALUMINUM; MICROSTRUCTURE; DISSOLUTION; DELTA;
D O I
10.1016/j.actamat.2014.04.027
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The room temperature cyclic deformation behaviour of an Al-Zn-Mg-(Cu) alloy was examined in the under-aged and peak-aged states. The tests were performed under constant plastic strain amplitude loading in tension compression mode, and the effect of cumulative strain (number of cycles), strain rate and plastic strain amplitude was examined. Pronounced cyclic hardening was observed in the under-aged states, and characterization of the microstructure using small-angle X-ray scattering illustrated that this was due to profuse dynamic precipitation at room temperature during cycling. Regardless of deformation conditions, the radius of the dynamically formed GP zones remained constant at 4-5 angstrom, and only the volume fraction of the zones increased during cycling. The strain, strain rate and plastic strain amplitude dependence of the evolution of the volume fraction of zones forming dynamically was interpreted in terms of a nucleation-dominated reaction, and it is shown that the behaviour can be satisfactorily rationalized when the role of strain-induced vacancies is considered. (C) 2014 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
引用
收藏
页码:96 / 109
页数:14
相关论文
共 53 条
[21]   Evolution of Precipitate Microstructure During Creep of an AA7449 T7651 Aluminum Alloy [J].
Fribourg, G. ;
Brechet, Y. ;
Chemin, J. L. ;
Deschamps, A. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2011, 42A (13) :3934-3940
[22]   On the coupling between precipitation and plastic deformation in relation with friction stir welding of AA2024 T3 aluminium alloy [J].
Genevois, Cecile ;
Fabregue, Damien ;
Deschamps, Alexis ;
Poole, Waffen J. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 441 (1-2) :39-48
[23]   Dynamic precipitation during cyclic deformation of an underaged Al-Cu alloy [J].
Han, W. Z. ;
Chen, Y. ;
Vinogradov, A. ;
Hutchinson, C. R. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (24) :7410-7416
[24]   On the reversibility of dislocation slip during cyclic deformation of Al alloys containing shear-resistant particles [J].
Han, W. Z. ;
Vinogradov, A. ;
Hutchinson, C. R. .
ACTA MATERIALIA, 2011, 59 (09) :3720-3736
[25]   Aluminium in Innovative Light-Weight Car Design [J].
Hirsch, Juergen .
MATERIALS TRANSACTIONS, 2011, 52 (05) :818-824
[26]   Quantifying the strain-induced dissolution of precipitates in Al alloy microstructures using nuclear magnetic resonance [J].
Hutchinson, C. R. ;
Loo, P. T. ;
Bastow, T. J. ;
Hill, A. J. ;
Teixeira, J. da Costa .
ACTA MATERIALIA, 2009, 57 (19) :5645-5653
[27]   CHEMICAL-ANALYSIS OF PERSISTENT SLIP BANDS IN AN AGE-HARDENED ALUMINUM-SILVER ALLOY BY MEANS OF EDS [J].
KOHLER, E ;
BISCHOFF, E ;
GEROLD, V .
SCRIPTA METALLURGICA, 1984, 18 (07) :699-702
[28]  
Larche F. C., 1979, Dislocations in solids, vol.IV. Dislocations in metallurgy, P135
[29]  
Lumley R.N., 2005, Materials Forum, V29, P256
[30]   Evolution of precipitate microstructures during the retrogression and re-ageing heat treatment of an Al-Zn-Mg-Cu alloy [J].
Marlaud, T. ;
Deschamps, A. ;
Bley, F. ;
Lefebvre, W. ;
Baroux, B. .
ACTA MATERIALIA, 2010, 58 (14) :4814-4826