Quantitative measurements of dynamic precipitation during fatigue of an Al-Zn-Mg-(Cu) alloy using small-angle X-ray scattering

被引:102
作者
Hutchinson, C. R. [1 ]
de Geuser, F. [2 ,3 ]
Chen, Y. [1 ,4 ]
Deschamps, A. [2 ,3 ]
机构
[1] Monash Univ, Dept Mat Engn, ARC Ctr Excellence Design Light Met, Clayton, Vic 3168, Australia
[2] Univ Grenoble Alpes, SIMAP, F-38000 Grenoble, France
[3] CNRS, SIMAP, F-38000 Grenoble, France
[4] Monash Univ, Monash Ctr Electron Microscopy, Clayton, Vic 3168, Australia
基金
澳大利亚研究理事会; 欧洲研究理事会;
关键词
Dynamic precipitation; Cyclic deformation; Fatigue; 7xxx; Small-angle X-ray scattering; ZN-MG ALLOY; PERSISTENT SLIP BANDS; CYCLIC DEFORMATION; PLASTIC-DEFORMATION; VOLUME FRACTION; ATOM-PROBE; ALUMINUM; MICROSTRUCTURE; DISSOLUTION; DELTA;
D O I
10.1016/j.actamat.2014.04.027
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The room temperature cyclic deformation behaviour of an Al-Zn-Mg-(Cu) alloy was examined in the under-aged and peak-aged states. The tests were performed under constant plastic strain amplitude loading in tension compression mode, and the effect of cumulative strain (number of cycles), strain rate and plastic strain amplitude was examined. Pronounced cyclic hardening was observed in the under-aged states, and characterization of the microstructure using small-angle X-ray scattering illustrated that this was due to profuse dynamic precipitation at room temperature during cycling. Regardless of deformation conditions, the radius of the dynamically formed GP zones remained constant at 4-5 angstrom, and only the volume fraction of the zones increased during cycling. The strain, strain rate and plastic strain amplitude dependence of the evolution of the volume fraction of zones forming dynamically was interpreted in terms of a nucleation-dominated reaction, and it is shown that the behaviour can be satisfactorily rationalized when the role of strain-induced vacancies is considered. (C) 2014 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
引用
收藏
页码:96 / 109
页数:14
相关论文
共 53 条
[1]  
AARONSON HI, 1999, LECT THEORY PHASE TR, P165
[2]  
[Anonymous], 2008, ASM Handbook
[3]  
[Anonymous], 1971, STRENGTHENING METHOD
[4]   HIGH-TEMPERATURE CYCLIC DEFORMATION OF PRECIPITATION HARDENED ALLOY .1. PARTIALLY COHERENT PRECIPITATES [J].
BHAT, SP ;
LAIRD, C .
ACTA METALLURGICA, 1979, 27 (12) :1861-1871
[5]   EXPERIMENTAL (TEM AND STEM) INVESTIGATION AND THEORETICAL APPROACH TO THE FATIGUE-INDUCED DISSOLUTION OF DELTA' PRECIPITATES IN A 2.5 WT-PERCENT AL-LI ALLOY [J].
BRECHET, Y ;
LOUCHET, F ;
MARCHIONNI, C ;
VERGERGAUGRY, JL .
PHILOSOPHICAL MAGAZINE A-PHYSICS OF CONDENSED MATTER STRUCTURE DEFECTS AND MECHANICAL PROPERTIES, 1987, 56 (03) :353-366
[6]  
BROOM T, 1956, J I MET, V84, P357
[7]   THE EFFECT OF PLASTIC-DEFORMATION ON AL2CULI (T1) PRECIPITATION [J].
CASSADA, WA ;
SHIFLET, GJ ;
STARKE, EA .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1991, 22 (02) :299-306
[8]   CYCLIC STRAIN INDUCED PRECIPITATION IN A SOLUTION TREATED ALUMINUM-ALLOY [J].
CHANDLER, HD ;
BEE, JV .
ACTA METALLURGICA, 1987, 35 (10) :2503-2510
[9]   The effect of interrupted aging on the yield strength and uniform elongation of precipitation-hardened Al alloys [J].
Chen, Y. ;
Weyland, M. ;
Hutchinson, C. R. .
ACTA MATERIALIA, 2013, 61 (15) :5877-5894
[10]  
Damask A.C., 1963, Point Defects in Metals