Influence of ferritic nitrocarburizing on the high-temperature corrosion-fatigue properties of the Si-Mo-Al cast iron SiMo1000

被引：10

作者：

Xiang, Shengmei ^{[1
]}

Jonsson, Stefan ^{[1
]}

Hedstrom, Peter ^{[1
]}

Zhu, Baohua ^{[2
]}

Odqvist, Joakim ^{[1
]}

机构：

[1] KTH, Royal Inst Technol, Dept Mat Sci & Engn, SE-10044 Stockholm, Sweden

[2] Scania CV AB, Mat Technol, S-15187 Sodertalje, Sweden

来源：

INTERNATIONAL JOURNAL OF FATIGUE | 2021年 / 143卷

关键词：

Corrosion fatigue; Cast iron; High temperature; Controlled atmosphere; Ferritic nitrocarburizing; THERMOMECHANICAL FATIGUE; BEHAVIOR; NITRIDE; ALLOYS;

D O I：

10.1016/j.ijfatigue.2020.105984

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

The influence of ferritic nitrocarburizing on the high-temperature corrosion-fatigue properties of the Si-Mo-Al cast iron SiMo1000 is investigated in the present study. It was found that nitrocarburizing effectively increases the surface hardness, but dramatically decreases the fatigue and oxidation resistance of SiMo1000. The fatigue resistance is reduced due to two types of microcracks formed after nitrocarburizing. The oxidation resistance is dramatically diminished due to the formation of microcracks, and the depletion of aluminum in the matrix from nitride precipitation during the exposure at 800 degrees C. The corrosion-fatigue synergy is found to cause severe decarburization (i.e. graphite depletion) in nitrocarburized SiMo1000.

引用

页数：14

共 45 条

[1] ahner P, 2006, VALIDATED CODE OF PR
[2] Life assessment of SiMo 4.06 cast iron under LCF and TMF loading conditions
Bartosak, M.
Novotny, C.
Spaniel, M.
Doubrava, K.
[J]. MATERIALS AT HIGH TEMPERATURES, 2019, 36 (04) : 285 - 295
[3] Basquin O.H., 1910, ASTM, V10, P625
[4] Effect of graphite morphology on the fatigue and fracture resistance of ferritic ductile cast iron
Benedetti, M.
Fontanari, V
Lusuardi, D.
[J]. ENGINEERING FRACTURE MECHANICS, 2019, 206 : 427 - 441
[5] Campbell F.C., 2008, Elements of Metallurgy and Engineering Alloys
[6] Thermal and microstructural characterization of a novel ductile cast iron modified by aluminum addition
Celik, Gulsah Aktas
Tzini, Maria-Ioanna T.
Polat, Seyda
Atapek, S. Hakan
Haidemenopoulos, Gregory N.
[J]. INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2020, 27 (02) : 190 - 199
[7] An energetic approach in thermomechanical fatigue for silicon molybdenum cast iron
Charkaluk, E
Constantinescu, A
[J]. MATERIALS AT HIGH TEMPERATURES, 2000, 17 (03) : 373 - 380
[8] Coffin J., 1954, T AM SOC MECH ENG, V76, P931
[9] EFFECT OF HIGH-VACUUM ON LOW-CYCLE FATIGUE LAW
COFFIN, LF
[J]. METALLURGICAL TRANSACTIONS, 1972, 3 (07): : 1777 - &
[10] COLIJN PF, 1983, Z METALLKD, V74, P620

← 1 2 3 4 5 →