Formation of Hydrogels Based on a Copolymer of N-Vinyl-2-pyrrolidone and Glycidyl Methacrylate in the Presence of the Reaction Product of 1,3-Dimethylmidazolium Dimethylphosphate and Elemental Sulfur

The aim of the study is to search for a reaction that provides the possibility of tandem "one-pot" formation of polymer networks during radical copolymerization of N-vinyl-2-pyrrolidone and glycidyl methacrylate. It was shown that the addition of recently synthesized 1,3-dimethylimidazolium (phosphonooxy-)oligosulfanide makes it possible to obtain a cross-linked copolymer in one stage as a result of radical copolymerization of N-vinyl-2-pyrrolidone and glycidyl methacrylate with a molar ratio of monomers less than 1.4. The structure of the copolymerization products of N-vinyl-2-pyrroldione and glycidyl methacrylate formed in the presence of 1,3-dimethylimidazolium (phosphonooxy-)oligosulfanide was characterized by H-1 NMR, FTIR and MALDI spectroscopy. H-1 NMR spectroscopy revealed an interaction under moderate heating between glycidyl methacrylate and 1,3-dimethylimidazolium (phosphonooxy-)oligosulfanide, accompanied by the formation of a mixture of unsaturated products of complex structure, presumably acting as crosslinking agents. It is shown that when the molar ratio of N-vinyl-2-pyrroldione/glycidyl methacrylate comonomers is 0.89, a densely crosslinked copolymer is formed, capable of limited swelling in water with a velocity constant of 5.06 x 10(-2) min(-1) and an equilibrium degree of swelling of about 227%.