From micro- to macroplasticity

被引：81

作者：

Brandstetter, Stefan ^{[1
]}

Van Swygenhoven, Helena ^{[1
]}

Van Petegem, Steven ^{[1
]}

Schmitt, Bernd ^{[1
]}

Maass, Robert ^{[1
]}

Derlet, Peter M. ^{[1
]}

机构：

[1] Paul Scherrer Inst, CH-5232 Villigen, Switzerland

来源：

ADVANCED MATERIALS | 2006年 / 18卷 / 12期

关键词：

D O I：

10.1002/adma.200600397

中图分类号：

O6 [化学];

学科分类号：

0703 ;

摘要：

The microplastic regime, where materials exhibit plastic deformation at stresses well below the yield stress, is of great importance for the precise design of functional materials. In polycrystalline metals, it is taken for granted that the majority of grains are plastically deforming at the macroscopic yield stress; however, there is no easy method to verify this assumption. The figure shows that for electrodeposited nanocrystalline Ni the usual 0.2 % definition of yield stress does not correspond with the onset of macroscopic plasticity.

引用

页码：1545 / +

页数：5

共 29 条

[1] American society for testing and materials [ASTM], 2004, STAND TEST METH TENS
[2] DEFORMATION OF PLASTICALLY NON-HOMOGENEOUS MATERIALS
ASHBY, MF
[J]. PHILOSOPHICAL MAGAZINE, 1970, 21 (170): : 399 - &
[3] MICROSTRAIN IN POLYCRYSTALLINE METALS
BROWN, N
LUKENS, KF
[J]. ACTA METALLURGICA, 1961, 9 (02): : 106 - 111
[4] Footprints of deformation mechanisms during in situ x-ray diffraction:: Nanocrystalline and ultrafine grained Ni -: art. no. 231910
Budrovic, Z
Van Petegem, S
Derlet, PM
Schmitt, B
Van Swygenhoven, H
Schafler, E
Zehetbauer, M
[J]. APPLIED PHYSICS LETTERS, 2005, 86 (23) : 1 - 3
[5] Plastic deformation with reversible peak broadening in nanocrystalline nickel
Budrovic, Z
Van Swygenhoven, H
Derlet, PM
Van Petegem, S
Schmitt, B
[J]. SCIENCE, 2004, 304 (5668) : 273 - 276
[6] CAPULONGO L, 2005, T ASME, V127, P400
[7] Plastic heterogeneities of a copper multicrystal deformed in uniaxial tension: Experimental study and finite element simulations
Delaire, F
Raphanel, JL
Rey, C
[J]. ACTA MATERIALIA, 2000, 48 (05) : 1075 - 1087
[8] INTERNAL-FRICTION AND MICRODEFORMATION DUE TO THE INTRINSIC-PROPERTIES OF DISLOCATIONS - THE BORDONI RELAXATION
FANTOZZI, G
ESNOUF, C
BENOIT, W
RITCHIE, IG
[J]. PROGRESS IN MATERIALS SCIENCE, 1982, 27 (3-4) : 311 - 451
[9] Computational description of nanocrystalline deformation based on crystal plasticity
Fu, HH
Benson, DJ
Meyers, MA
[J]. ACTA MATERIALIA, 2004, 52 (15) : 4413 - 4425
[10] Hirth J. P., 1982, THEORY DISLOCATIONS

← 1 2 3 →