Effect of cold-rolling strain on the evolution of annealing texture of equiatomic CoCrFeMnNi high entropy alloy

被引:70
作者
Sathiaraj, G. Dan [1 ]
Bhattacharjee, P. P. [1 ]
机构
[1] Indian Inst Technol, Dept Mat Sci & Met Engn, Hyderabad, Andhra Pradesh, India
关键词
High entropy alloys; Cold-rolling; Annealing; Microstructure; Texture; EBSD; MECHANICAL-PROPERTIES; PHASE-STABILITY; GRAIN-GROWTH; SINGLE-PHASE; MICROSTRUCTURE; DEPENDENCE; RECRYSTALLIZATION; DEFORMATION; PLASTICITY; BEHAVIOR;
D O I
10.1016/j.matchar.2015.09.027
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The effect of cold-rolling strain on the evolution of microstructure and texture during annealing was studied in an equiatomic CoCrFeMnNi high entropy alloy. For this purpose the alloy was cold-rolled to 60%, 80% and 95% reduction in thickness. The three cold-rolled materials were isochronally annealed for 1 hat temperatures ranging between 700 degrees C and 1200 degrees C. With increasing rolling reduction, the texture transition from pure metal type (<60% reduction) to an alloy type texture (>80% reduction) was observed. The final recrystallized grain size was found to decrease systematically with increasing prior cold-rolling strain. However, the effect was much less pronounced below the annealing temperature of 1200 degrees C due to sluggish diffusion in the HEA. The recrystallization texture of different deformed materials showed the presence of similar texture components indicating that prior deformation had only limited effect on the formation of annealing texture. The typical annealing texture components of low SFE materials, such as {236}< 385 > or {113}< 332 > were not the dominant components. The volume fractions of different texture components also did not reveal significant dependence on the annealing temperature. The evolution of annealing texture in the HEA could be adequately explained by the absence of strong preferential nucleation and growth. (C) 2015 Elsevier Inc. All rights reserved.
引用
收藏
页码:189 / 197
页数:9
相关论文
共 44 条
  • [1] Temperature Effects on Deformation and Serration Behavior of High-Entropy Alloys (HEAs)
    Antonaglia, J.
    Xie, X.
    Tang, Z.
    Tsai, C. -W.
    Qiao, J. W.
    Zhang, Y.
    Laktionova, M. O.
    Tabachnikova, E. D.
    Yeh, J. W.
    Senkov, O. N.
    Gao, M. C.
    Uhl, J. T.
    Liaw, P. K.
    Dahmen, K. A.
    [J]. JOM, 2014, 66 (10) : 2002 - 2008
  • [2] Experimental Determination and Simulation of Annealing Textures in Cold Rolled TWIP and TRIP Steels
    Barrales-Mora, L. A.
    Lue, Y.
    Molodov, D. A.
    [J]. STEEL RESEARCH INTERNATIONAL, 2011, 82 (02) : 119 - 126
  • [3] Microstructure and texture evolution during annealing of equiatomic CoCrFeMnNi high-entropy alloy
    Bhattacharjee, P. P.
    Sathiaraj, G. D.
    Zaid, M.
    Gatti, J. R.
    Lee, Chi
    Tsai, Che-Wei
    Yeh, Jien-Wei
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2014, 587 : 544 - 552
  • [4] Microstructure and texture evolution during cold rolling and annealing of a high Mn TWIP steel
    Bracke, L.
    Verbeken, K.
    Kestens, L.
    Penning, J.
    [J]. ACTA MATERIALIA, 2009, 57 (05) : 1512 - 1524
  • [5] Texture generation and implications in TWIP steels
    Bracke, Lieven
    Verbeken, Kim
    Kestens, Leo A. I.
    [J]. SCRIPTA MATERIALIA, 2012, 66 (12) : 1007 - 1011
  • [6] Recrystallization and texture
    Doherty, RD
    [J]. PROGRESS IN MATERIALS SCIENCE, 1997, 42 (1-4) : 39 - 58
  • [7] Duggan B. J., 1998, ICOTOM 8, P625
  • [8] A fracture-resistant high-entropy alloy for cryogenic applications
    Gludovatz, Bernd
    Hohenwarter, Anton
    Catoor, Dhiraj
    Chang, Edwin H.
    George, Easo P.
    Ritchie, Robert O.
    [J]. SCIENCE, 2014, 345 (6201) : 1153 - 1158
  • [9] Steady state flow of the FeCoNiCrMn high entropy alloy at elevated temperatures
    He, J. Y.
    Zhu, C.
    Zhou, D. Q.
    Liu, W. H.
    Nieh, T. G.
    Lu, Z. P.
    [J]. INTERMETALLICS, 2014, 55 : 9 - 14
  • [10] Fatigue behavior of Al0.5CoCrCuFeNi high entropy alloys
    Hemphill, M. A.
    Yuan, T.
    Wang, G. Y.
    Yeh, J. W.
    Tsai, C. W.
    Chuang, A.
    Liaw, P. K.
    [J]. ACTA MATERIALIA, 2012, 60 (16) : 5723 - 5734