Investigation of microstructure and mechanical properties of semi-solid state joining of SSM aluminum alloys

被引：2

作者：

Petkhwan, Apirit ^{[1
]}

Muangjunburee, Prapas ^{[1
]}

Wannasin, Jessada ^{[1
]}

机构：

[1] Prince Songkla Univ, Fac Engn, Dept Min & Mat Engn, Hat Yai 90112, Thailand

来源：

FRONTIERS OF MANUFACTURING AND DESIGN SCIENCE IV, PTS 1-5 | 2014年 / 496-500卷

关键词：

SSM A356 Aluminum Alloy; Semi-Solid Metal; Semi-Solid Joining;

D O I：

10.4028/www.scientific.net/AMM.496-500.371

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In this research, the semi-solid state joining of SSM A356 aluminum alloy was investigated. The butt-joint of SSM A356 was heated by an induction heating coil to create a localized semisolid pool. Then a stirrer was applied into the joint seam in order to mix the weld metal. The accurate controlling of temperature during joining was measured. The effects of stirring rate on physical, macrostructure, microstructure and mechanical properties were studied. Experimental results showed that increase in stirring rates, the surface of the joint was smooth. The weld metal consisted of the globular microstructure and also voids. The density of weld metal zone increased by an appropriate stirring. The best tensile strength was achieved with 1750 rpm, 70 mm/min for 103.4 MPa.

引用

页码：371 / 375

页数：5

共 7 条

[1] Effect of pre/post T6 heat treatment on the mechanical properties of laser welded SSM cast A356 aluminium alloy
Akhter, R.
Ivanchev, L.
Burger, H. P.
[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2007, 447 (1-2): : 192 - 196
[2] Semisolid joining of aluminum A356 alloy by partial remelting and mechanical stirring
Alvani, S. M. J.
Aashuri, H.
Kokabi, A.
Beygi, R.
[J]. TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2010, 20 (09) : 1792 - 1798
[3] Boonchouytan W., 2012, ADV MAT RES, V488, P328, DOI [10.4028/www.scientific.net/AMR.488-489.328, DOI 10.4028/WWW.SCIENTIFIC.NET/AMR.488-489.328]
[4] Burapa Romadorn, 2009, PSU E ENG C PEC 5 21
[5] Microstructural evolution and mechanical properties of semisolid stir welded zinc AG40A die cast alloy
Narimannezhad, A.
Aashuri, H.
Kokabi, A. H.
Khosravani, A.
[J]. JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2009, 209 (08) : 4112 - 4121
[6] Microstructure and Properties of Joint Interface of Semisolid Stirring Brazing of Composites
Xu, Huibin
Zhou, Bofang
Du, Changhua
Luo, Quanxiang
Chen, Hongyou
[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2012, 28 (12) : 1163 - 1168
[7] The effect of stirring rate on semisolid stirring brazing of SiCp/A356 composites in air
Xu, Huibin
Luo, Quanxiang
Zhou, Bofang
Zeng, Youliang
Du, Changhua
[J]. MATERIALS & DESIGN, 2012, 34 : 452 - 458

← 1 →