Variations of conductivities of NaOH-KOH molten salt during the process of synthesis of BaTiO3

被引：0

作者：

Bai, YX ^{[1
]}

Wang, SL ^{[1
]}

Li, Y ^{[1
]}

机构：

[1] Northeastern Univ, Shenyang, Peoples R China

来源：

JOURNAL OF INORGANIC MATERIALS | 2002年 / 17卷 / 03期

关键词：

BaTiO3; conductivity; NaOH-KOH eutectic salt;

D O I：

暂无

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The conductivities of eutectic NaOH-KOH molten salt during the process of forming BaTiO3 from BaCO3 and TiO2 were measured by A.C. impedance method at 350degreesC. Results showed that the accurate conductivity of eutectic NaOH-KOH molten salt at 350degreesC was 1.053Omega(-1).cm(-1). The dissolution of BaCO3 and TiO2 in NaOH-KOH of eutectic component at 350degreesC reached equilibrium in a short time, and NaOH and KOH did not react with BaCO3 and TiO2 at 350degreesC.

引用

页码：609 / 612

页数：4

共 6 条

[1] MOLTEN-SALT SYNTHESIS OF SINGLE MAGNETIC DOMAIN BAFE12O19 AND SRFE12O19 CRYSTALS
ARENDT, RH
[J]. JOURNAL OF SOLID STATE CHEMISTRY, 1973, 8 (04) : 339 - 347
[2] ARENDT RH, 1987, CERAMIC ELECTROLYTE, V134, P733
[3] Synthesis of oxide perovskite solid solutions using the molten salt method
Gopalan, S
Mehta, K
Virkar, AV
[J]. JOURNAL OF MATERIALS RESEARCH, 1996, 11 (08) : 1863 - 1865
[4] FORMATION OF LEAD NIOBATES IN MOLTEN-SALT SYSTEMS
LI, CC
CHIU, CC
DESU, SB
[J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1991, 74 (01) : 42 - 47
[5] High-accuracy, calibration-free technique for measuring the electrical conductivity of molten oxides
Schiefelbein, SL
Sadoway, DR
[J]. METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 1997, 28 (06): : 1141 - 1149
[6] The conductivity and the crystallization of perovskite (CaTiO3) from Ti-bearing blast furnace slag studied by A. C. impedance method
Wang, SL
Li, GQ
Lou, TP
Sui, ZT
[J]. ISIJ INTERNATIONAL, 1999, 39 (11) : 1116 - 1119

← 1 →