X-RAY DIFFRACTION STUDY OF MICROSTRUCTURAL CHANGES DURING FATIGUE DAMAGE INITIATION IN STEEL PIPES

被引:0
作者
Pinheiro, Bianca [1 ]
Lesage, Jacky [1 ]
Pasqualino, Ilson
Benseddiq, Noureddine [1 ]
Bemporad, Edoardo
机构
[1] Univ Lille 1, Lab Mech Lille, Lille, France
来源
PROCEEDINGS OF THE 9TH INTERNATIONAL PIPELINE CONFERENCE - 2012, VOL 3 | 2013年
关键词
RESIDUAL-STRESS RELAXATION; LOW-CYCLE FATIGUE; AISI; 4140; STEEL; STAINLESS-STEEL; STRENGTH; STABILITY; BEHAVIOR; TEMPERATURES; DEFORMATION; PRESSURE;
D O I
暂无
中图分类号
TE [石油、天然气工业];
学科分类号
0820 ;
摘要
The present work aims to evaluate the microstructural mechanisms associated with the initiation of fatigue damage in steels used in the petroleum industry. Microdeformations and residual stresses (macrostresses) are evaluated by X-ray diffraction in real time during alternating bending fatigue tests performed on samples taken from an API 5L X60 grade steel pipe. Microdeformations are evaluated from measurements of the full width at half maximum (FWHM) of the diffraction peak and residual stresses are estimated from the peak displacement. The evolution of microdeformations shows three regular successive stages of changes. The amplitude of variation of each stage is intensified with increasing stress amplitude, while the duration is reduced. A similar evolution is found for residual stresses, whose stages of changes have nearly the same durations as those of microdeformations. Changes in density and distribution of dislocations are observed by transmission electron microscopy combined with the technique of focused ion beam. To understand the role of the initial structure, fatigue tests on annealed samples are performed under the same test conditions. Again, three stages of changes are observed, but with an increase in microdeformations instead of a decrease during the first stage due to the initial state of the dislocation network. The results are very encouraging for the consideration of microstructural changes measured by X-ray diffraction in the development of a future indicator of fatigue damage initiation in API 5L X60 grade steel pipes.
引用
收藏
页码:661 / 670
页数:10
相关论文
共 51 条
[31]   Residual stress relaxation of deep-rolled austenitic steel [J].
Nikitin, I. ;
Besel, M. .
SCRIPTA MATERIALIA, 2008, 58 (03) :239-242
[32]   Comparison of the fatigue behavior and residual stress stability of laser-shock peened and deep rolled austenitic stainless steel AISI 304 in the temperature range 25-600°C [J].
Nikitin, I. ;
Altenberger, I. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2007, 465 (1-2) :176-182
[33]  
Nikitin I., 2004, SCRIPTA MATER, V50, P1345
[34]  
Nikitin I., 2008, MAT SCI ENG A-STRUCT, V491, P297
[35]   Ultrasonic attenuation peak in steel and aluminum alloy during rotating bending fatigue [J].
Ogi, H ;
Hamaguchi, T ;
Hirao, M .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2000, 31 (04) :1121-1128
[36]   Fatigue damage assessment in AISI 8620 steel using Barkhausen noise [J].
Palma, ES ;
Mansur, TR ;
Silva, SF ;
Alvarenga, A .
INTERNATIONAL JOURNAL OF FATIGUE, 2005, 27 (06) :659-665
[37]  
Paulson K., 2005, COMP ANAL PIPELINE P
[38]  
Pc P., 1961, Trend Eng., V13, P9
[39]   X-ray diffraction study of microstructural changes during fatigue damage initiation in steel pipes [J].
Pinheiro, B. ;
Lesage, J. ;
Pasqualino, I. ;
Benseddiq, N. ;
Bemporad, E. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 532 :158-166
[40]  
Pinheiro B., 2011, P 30 INT C OC OFFSH