Intermediate temperature embrittlement of copper alloys

被引:75
作者
Laporte, V. [1 ]
Mortensen, A. [1 ]
机构
[1] Ecole Polytech Fed Lausanne, Lab Mech Met, Inst Mat, Stn 12, CH-1015 Lausanne, Switzerland
关键词
Copper; Ductility; Intergranular fracture; Grain boundary embrittlement; Liquid metal embrittlement; Metal-induced embrittlement; GRAIN-BOUNDARY SEGREGATION; STRAIN-RATE DEPENDENCE; LIQUID-METAL EMBRITTLEMENT; DEFORMATION PROCESSING MAP; BRITTLE INTERGRANULAR FRACTURE; DUCTILITY MINIMUM TEMPERATURE; BISMUTH-INDUCED EMBRITTLEMENT; STACKING-FAULT ENERGY; PERCENT SN ALLOY; NI-ZN ALLOYS;
D O I
10.1179/174328009X392967
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Copper and its alloys generally display a severe reduction in ductility between roughly 300 and 600 degrees C, a phenomenon variously called 'intermediate temperature embrittlement' or 'ductility trough behaviour'. This review of the phenomenon begins by placing it in the wider context of the high-temperature fracture of metals, showing how its occurrence can be rationalised in simple terms on the basis of what is known of intergranular creep fracture and dynamic recrystallisation. Data in the literature are reviewed to identify main causes and mechanisms for embrittlement, first for pure copper, and then for monophase and multiphase copper alloys. Coverage then turns to the 'grain boundary embrittlement' phenomenon, caused by the intergranular segregation of even minute quantities of alloying additions or impurities, which appears to worsen dramatically the intermediate temperature embrittlement of copper alloys. Finally, metal-induced embrittlement, including in particular liquid metal embrittlement, is presented as a second mechanism leading to an exacerbation of the intermediate temperature embrittlement of copper and its alloys.
引用
收藏
页码:94 / 116
页数:23
相关论文
共 362 条
[11]   GRAIN-BOUNDARY CREEP IN COPPER [J].
AYENSU, A ;
QUAINOO, GK ;
ADJEPONG, SK .
JOURNAL OF MATERIALS SCIENCE LETTERS, 1993, 12 (13) :1008-1010
[12]   The inter-relationship between grain boundary sliding and cavitation during creep of polycrystalline copper [J].
Ayensu, A ;
Langdon, TG .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1996, 27 (04) :901-907
[13]  
BAKER WA, 1949, J I MET, V75, P741
[14]   QUASI-STATIC INTERGRANULAR CRACKING IN A CU-SN ALLOY - AN ANALOG OF STRESS RELIEF CRACKING OF STEELS [J].
BARRERA, EV ;
MENYHARD, M ;
BIKA, D ;
ROTHMAN, B ;
MCMAHON, CJ .
SCRIPTA METALLURGICA ET MATERIALIA, 1992, 27 (02) :205-210
[15]   GAS-PHASE EMBRITTLEMENT BY METAL VAPORS [J].
BECKMAN, JP ;
WOODFORD, DA .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1989, 20 (01) :184-188
[16]   Strain-induced grain evolution in polycrystalline copper during warm deformation [J].
Belyakov, A ;
Gao, W ;
Miura, H ;
Sakai, T .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1998, 29 (12) :2957-2965
[17]   A COMBINED EXPERIMENTAL AND ANALYTICAL INVESTIGATION OF CREEP DAMAGE DEVELOPMENT IN COPPER [J].
BENCI, JE ;
POPE, DP ;
BASSANI, JL .
ACTA METALLURGICA ET MATERIALIA, 1994, 42 (01) :225-238
[18]   EFFECT OF INTERFACIAL SULFUR SEGREGATION ON THE HOT DUCTILITY DROP OF FE-NI36 ALLOYS [J].
BENMOSTEFA, L ;
SAINDRENAN, G ;
SOLIGNAC, MP ;
COLIN, JP .
ACTA METALLURGICA ET MATERIALIA, 1991, 39 (12) :3111-3118
[19]   A MODEL FOR DYNAMIC EMBRITTLEMENT [J].
BIKA, D ;
MCMAHON, CJ .
ACTA METALLURGICA ET MATERIALIA, 1995, 43 (05) :1909-1916
[20]  
BLAZ L, 1989, MATER SCI TECH SER, V5, P1186, DOI 10.1179/026708389790222212