Ultra-high cycle fatigue behavior of high strength steel with carbide-free bainite/martensite complex microstructure

被引：14

作者：

Xu, Xue-xia ^{[1
]}

Yu, Yang ^{[1
]}

Cui, Wen-long ^{[1
]}

Bai, Bing-zhe ^{[1
]}

Gu, Jia-lin ^{[1
]}

机构：

[1] Tsinghua Univ, Dept Mat Sci & Engn, Adv Mat Lab, Beijing 100084, Peoples R China

来源：

INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS | 2009年 / 16卷 / 03期

关键词：

high strength steel; ultra-high cycle fatigue; bainite; martensite; fatigue behavior; CRACK INITIATION; MECHANISM; FAILURE; LIMIT; LIFE;

D O I：

10.1016/S1674-4799(09)60051-0

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The ultra-high cycle fatigue behavior of a novel high strength steel with carbide-free bainite/martensite (CFB/M) complex microstructure was studied. The ultra-high cycle fatigue properties were measured by ultrasonic fatigue testing equipment at a frequency of 20 kHz. It is found that there is no horizontal part in the S-N curve and fatigue fracture occurs when the life of specimens exceeds 10(7) Cycles. In addition, the origination of fatigue cracks tends to transfer from the surface to interior of specimens as the fatigue cycle exceeds 10(7), and the fatigue crack originations of many specimens are not induced by inclusions, but by some kind of "soft structure". It is shown that the studied high strength steel performs good ultra-high cycle fatigue properties. The ultra-high fatigue mechanism was discussed and it is suggested that specific CFB/M complex microstructure of the studied steel contributes to its superior properties.

引用

页码：285 / 292

页数：8

共 18 条

[1]

Bathias C, 1999, FATIGUE FRACT ENG M, V22, P559, DOI 10.1046/j.1460-2695.1999.00183.x

[2]

Bathias C, 2001, INT J FATIGUE, V23, pS143, DOI 10.1016/S0142-1123(01)00123-2

[3] Multiaxial fatigue limit for defective materials: mechanisms and experiments [J].

Billaudeau, T ;

Nadot, Y ;

Bezine, G .

ACTA MATERIALIA, 2004, 52 (13) :3911-3920

[4] Ultra-long cycle fatigue of high-strength carbon steels part II: estimation of fatigue limit for failure from internal inclusions [J].

Chapetti, MD ;

Tagawa, T ;

Miyata, T .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 356 (1-2) :236-244

[5] Ultra-long cycle fatigue of high-strength carbon steels part I: review and analysis of the mechanism of failure [J].

Chapetti, MD ;

Tagawa, T ;

Miyata, T .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 356 (1-2) :227-235

[6] A novel 1500MPa economic high strength steel [J].

Gu, JL ;

Wei, DY ;

Chang, KD ;

Liu, DY ;

Fang, HS ;

Bai, BZ ;

Yang, ZG ;

Zhang, WZ .

THERMEC'2003, PTS 1-5, 2003, 426-4 :1475-1480

[7] 1980 INSTITUTE OF METALS LECTURE THE METALLURGICAL-SOCIETY-OF-AIME - EFFECTS OF HYDROGEN ON THE PROPERTIES OF IRON AND STEEL [J].

HIRTH, JP .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1980, 11 (06) :861-890

[8]

Kanazawa K., 1997, Journal of the Society of Materials Science, Japan, V46, P1396, DOI 10.2472/jsms.46.1396

[9]

MASUDA C, 1986, T JSME A, V52, P847, DOI DOI 10.1016/0036-9748(81)90340-9

[10] Factors influencing the mechanism of superlong fatigue failure in steels [J].

Murakami, Y ;

Nomoto, T ;

Ueda, T .

FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1999, 22 (07) :581-590

← 1 2 →