Experimental study on the behavior of glass/epoxy composite plate due to blast loading

被引:0
作者
Heriana [1 ]
Hadi, Bambang K. [1 ]
Widagdo, Djarot [1 ]
Kusni, Muh [1 ]
机构
[1] Inst Teknol Bandung, Fac Mech & Aerosp Engn, Bandung, Indonesia
来源
TARUMANAGARA INTERNATIONAL CONFERENCE ON THE APPLICATIONS OF TECHNOLOGY AND ENGINEERING | 2019年 / 508卷
关键词
D O I
10.1088/1757-899X/508/1/012060
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The paper discusses the effect of blast loading on the behavior of glass/epoxy composite plate. Woven glass fiber material was used. The composite plate was manufactured using hand lay-up method. The specimens consisted of 12 and 14 plies of woven glass fiber. A TNT explosive material was used. The TNT was in cylindrical shape without metal casting. The weight of TNT was varied, which are 60, 80 and 100 grams. The stand-off distance was 300, 500 and 1000 mm. The glass/epoxy specimen was placed on a rigid test table with fixed boundary conditions. The deflection was recorded using sewing pins in Styrofoam. The deflection contour was recorded, and the maximum deflection was 21 mm. All specimens survived the blast loading, although some delamination was observed after the test using TTU scan.
引用
收藏
页数:5
相关论文
共 11 条
[1]  
Abada M. M, 2016, P 11 INT C CIV ARCH
[2]  
Avachat S., 2015, THESIS
[3]   Blast resistance of unidirectional fiber reinforced composites [J].
Batra, R. C. ;
Hassan, N. M. .
COMPOSITES PART B-ENGINEERING, 2008, 39 (03) :513-536
[4]  
Burns G. N, 2011, 49 AIAA AER SCI M
[5]   Explosion Protection-Architectural Design, Urban Planning and Landscape Planning [J].
Gebbeken, Norbert ;
Doege, Torsten .
INTERNATIONAL JOURNAL OF PROTECTIVE STRUCTURES, 2010, 1 (01) :1-21
[6]  
Giversen S, 2014, S167 DCAMM DTU MACH
[7]   Deformation model and performance optimization research of composite blast resistant wall subjected to blast loading [J].
Liang, Xingxing ;
Wang, Zhongqi ;
Wang, Runan .
JOURNAL OF LOSS PREVENTION IN THE PROCESS INDUSTRIES, 2017, 49 :326-341
[8]  
Ngo T, 2007, ESJE SPECIAL ISSUE L
[9]  
Verma S., 2015, INT J RES ENG TECHNO, V4, P64
[10]   The response of carbon fibre composites to blast loading via the Europa CAFV programme [J].
Wright, Andy ;
French, Mark .
JOURNAL OF MATERIALS SCIENCE, 2008, 43 (20) :6619-6629