Studies of the positron lifetime and Doppler-broadened annihilation radiation of polypropylene-polystyrene alloys

Positron annihilation lifetime spectroscopy and Doppler-broadened annihilation radiation (DBAR) experiments were performed on polypropylene-polystyrene (PP-PS) alloys (0-100% styrene) prepared by in situ polymerisation of styrene in a PP host matrix. The mean size of free-volume holes estimated from the ortho-positronium lifetime tau(3) shows a continuous decrease from 0.119 nm(3) in PP to k0.095 nm(3) in PS. The intensity of the o-Ps component, I-3, the average positron lifetime tau(av), the curve-shape parameter S and the peak height H of the DBAR spectra increase linearly with the styrene concentration. This is attributed to a linear superposition of the Ps yields of PP and PS in the PP-PS alloys. The DBAR spectra were fitted by a sum of three Gaussians, the narrowest of them is attributed to self-annihilation of para-positronium confined within holes. After its subtraction. a 'broad component' is obtained which represents the momentum distribution of electrons bound to molecules. Its normatised peak height does not show any change with the composition which reflects the fact that both constituents of the PP-PS alloys contain only hydrogen and carbon atoms in their chemical units. Immersing of PP into styrene liquid leads to a very pronounced increases in the lifetime parameters which is attributed to the plasticisation of PP. (C) 2002 Elsevier Science Ltd. All rights reserved.